Phase Transformations and Electrochemical Characterizations of Electrodeposited Amorphous Fe–W Coatings

Song Wang,Cheng Zeng,Yunhan Ling,Jianjun Wang,Guiying Xu

DOI: https://doi.org/10.1016/j.surfcoat.2015.12.011

2016-01-01

Abstract:Iron–tungsten with satisfactory corrosion properties is a promising alloy to replace hard chromium. In this work, Fe–W amorphous coatings were prepared by electrodepositing from an aqueous solution and a subsequent heat treatment at 400°C, 500°C, 600°C, 700°C and 800°C, respectively. Corrosion behavior of the coatings deposited on copper substrates was studied using potentiodynamic polarization and impedance spectroscopy techniques in 0.1mol·L−1 aqueous NaCl solution. As the annealing temperature raises the corrosion resistance of Fe–W coatings increases, and reaches the maximum at 500°C and then shows a converse variation after 500°C. This might relate to the surface reconstruction both on the morphology and the chemical oxidation.