Abstract:NiCoCrAlY+(6–8wt%)Y2O3 stabilized ZrO2(YSZ) two-layer thermal barrier coatings (TBCs) were deposited by electron beam physical vapor deposition on Ni3Al or Ni-base superalloy and their high temperature fatigue behavior was investigated experimentally and computationally. It has been found that the pre-treatment of the bond coat has greatly improved the thermal cyclic lifetime of TBCs with respect to those without pre-treatment. The lifetime is limited by the existence of interface between bond coat and top coat, and smoothing the interface can also improve the thermal cyclic lifetime. When the roughness of the interface changed from 3.76 to 0.82μm, testing lifetime increased from about 500 (1000 cycles) to 700h (1400 cycles), and the adhesive strength of the interface increased from 3.5 to 4.7MPam1/2 estimated from the result of surface Rock-well hardness testing. Cracks occurred in the thermally grown oxide (TGO) layer are considered to be the main reason for the failure of two-layer TBCs. It has been found that with pre-oxide layer thickness increasing from 1.0 to 3.0μm, the growth rate of TGO increased during thermal cyclic testing and the thermal cyclic lifetime of TBCs decreased from 730 to 450h. The lower lifetime was caused by the co-action of larger internal stress resulted from thicker TGO layer and the fatigue of the TGO layer. Finite element method (FEM) analysis showed that large tensile stress was introduced at the beginning of rapid cooling process, resulting in the spallation of top coat from bond coat. Ab initio calculation was carried out to evaluate the binding energy of the interface of bond coat and ceramic top coat, and FEM models were used to investigate stress and strain states in TBCs during thermal shock process as a function of cooling rate. The results showed that ZrO2/Ni interface exhibits nonmetallic properties, and that the chemical bonding in ZrO2/Ni is covalent–ionic in nature. The calculation of binding energies between both Ni and O and Zr and O indicates that the binding energy of Ni and O is larger than that of Zr and O, which is helpful to investigate the failure mechanism of thermal barrier coatings.

Fractographic and microstructural study of isothermally and cyclically heat treated thermal barrier coatings

Microstructure and Thermal Cycling Behavior of Thermal Barrier Coating on Near-Α Titanium Alloy

Experimental and computational study on hot fatigue process of thermal barrier coatings by EB-PVD

Microstructure characteristics and deformation-induced crystalline-to-amorphous phase transformation in thermal barrier coatings during thermal cycling

Interfacial Fracture Toughness of APS Thermal Barrier Coating under High Temperature

Study of Failure of EB-PVD Thermal Barrier Coating Upon Near-Α Titanium Alloy

Microcracks characterization for thermal barrier coatings at high temperature

High Temperature In-Situ Synchrotron X-Ray Diffraction Technique of Thermal Barrier Coatings under Thermal Gradient and Mechanical Loads

Experimental Study on the Interfacial Delamination in a Thermal Barrier Coating System at Elevated Temperatures

Thermal Failure of Thermal Barrier Coating with Thermal Sprayed Bond Coating on Titanium Alloy

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Fracture Behavior of TBCs with Cooling Hole Structure under Cyclic Thermal Loadings

Preparing and Study of EB-PVD Thermal Barrier Coatings on Titanium Substrates

Thermal fatigue behavior of thermal barrier coatings with the MCrAlY bond coats by cold spraying and low-pressure plasma spraying

Microstructure Parameters Affecting Interfacial Adhesion of Thermal Barrier Coatings by the EB-PVD Method

Numerical Study on the Competitive Cracking Behavior in TC and Interface for Thermal Barrier Coatings under Thermal Cycle Fatigue Loading

Interfacial Fracture Toughness of APS Bond Coat/substrate under High Temperature

Performance of 2024 aluminum alloy thermal barrier coating systems subjected to elevated temperature fluctuation as a fatigue

Failure Behaviors of EB-PVD Thermal Barrier Coatings under Isothermal Oxidation and Thermal Cycling Conditions

Study on the Microstructure Evolution of Nano and Micron-size Thermal Barrier Coatings during Thermal Cycling

Cyclic Oxidation Behavior of Thermal Barrier Coatings in Environments Containing Water Vapor