Abstract:Emerging glass structures, which frequently use laminated glass (LG) as load bearing elements, see a significant rise in recent decade. Existing analytical solutions for LG under impact present limitation when introduced into structural LG products, as structural LG having more glass plies and soft polymeric interlayers requires more accurate nonlinear analytical model. In this study, a nonlinear analytical model was proposed for the simply supported square structural LG subjected to hard body impact. The motion equations were established based on a third order shear deformation theory and von Kármán nonlinear strain–displacement relationship. Based on a two-step perturbation method, the solutions of the motion equations were obtained. The fourth-order Runge–Kutta method was used to capture the impact force variation. Drop weight impact tests with increasing impact velocity, were conducted to record the impact force of LG panels before breakage. Eighteen LG panels with PVB or SG interlayers were tested. Through analysing the fracture initiation from high speed photos as well as the impact force variation in the impact attempt causing fracture, certain feature of the experimental impact force response was determined to be validated with analytical prediction. The validation results show that the proposed model can well reproduce the examined feature and achieve satisfactory impact force response. Case study was then designed to investigate the influence due to the safety windows film on reducing the pre-crack impact response. The effective thickness of LG based on the equivalence of indentation was also proposed for the hard body impact.

Finite Element Modelling of Impact Damage in Polyvinyl Butyral Laminated Glass

Modeling And Experimental Studies Of Crack Propagation In Laminated Glass Sheets

Impact Fracture Simulation of Laminated Glass Based on Thick Shell Elements and a Cohesive Zone Model

Deformation and Damage Mechanisms of Laminated Glass Windows Subjected to High Velocity Soft Impact

An Ordinary State-Based Peridynamic Modeling for Dynamic Fracture of Laminated Glass under Low-Velocity Impact

A finite element model for impact simulation with laminated glass

Soft Impact Response of Laminated Glass Plates

Simulating the Impact Damage of Laminated Glass Considering Mixed Mode Delamination Using FEM/DEM

An Analytical Model for Deformation and Damage of Rectangular Laminated Glass under Low-Velocity Impact

Investigation on Dynamic Propagation Characteristics of In-Plane Cracks in PVB Laminated Glass Plates

FEM/DEM Modelling of Hard Body Impact on the Laminated Glass

Investigation of Dynamic Multi-Cracking Behavior in PVB Laminated Glass Plates

Influences of temperature and impacting velocity on dynamic failure of laminated glass: Insights from peridynamic simulations

Experimental study on mechanical behavior of PVB laminated glass under quasi-static and dynamic loadings

Nonlinear analytical study of structural laminated glass under hard body impact in the pre-crack stage

Modeling Via Peridynamics for Crack Propagation in Laminated Glass under Fire

Parametric analyses on the impact fracture of laminated glass using the combined finite-discrete element method

Three-stage breakage model for laminated glass plate under low-velocity impact

Experimental and analytical study on the pre-crack impact response of thick multi-layered laminated glass under hard body impact

Combined Voronoi-FDEM Approach for Modelling Post-Fracture Response of Laminated Tempered Glass

Finite element analysis of dynamic progressive failure properties of GLARE hybrid laminates under low-velocity impact