Microstructure and Antiferroelectric-Like Behavior of PbxSr1−xTiO3 Ceramics
Hongwei Chen,Chuanren Yang,Jihua Zhang,Yafang Pei,Zhen Zhao
DOI: https://doi.org/10.1016/j.jallcom.2009.07.016
IF: 6.2
2009-01-01
Journal of Alloys and Compounds
Abstract:The crystalline structures of PbxSr1−xTiO3 ceramics with x=0.2–0.8 were investigated. The a- and c-axis lattice constants at room temperature were found not to be equal, corresponding to tetragonal phase when x≥0.45, consistent with the X-ray diffraction spectra. The hysteresis loops of PbxSr1−xTiO3 ceramics were measured in different conditions, including different Pb/Sr ratio, excess Pb, sintering temperature, and maximum external electric field. It is found that the PST ceramics for x=0.40 and 0.45 exhibit antiferroelectric-like behavior. For Pb0.45Sr0.55TiO3 ceramics, the antiferroelectric-like behavior enhanced as sintering temperature and maximum external electric field increased. Moreover, increasing excess lead content leads to abnormal hysteresis loops. The antiferroelectric-like behavior may be described in terms of the strongly stressed hybrid structure, domain pinning and oxygen vacancy.