Abstract:The Y, F, and Ag tridoped TiO2/SnO2 composite nanocrystalline film (YFAg–TS) with prominent photocatalytic performance was prepared by the modified sol–gel method and was characterized by utilizing X-ray diffraction (XRD), differential thermal and thermogravimetric (DTA–TG) analysis, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), Brunauer–Emmett–Teller (BET) method, ultraviolet–visible diffuse reflectance spectroscopy (UV–vis DRS), and photoluminescence (PL). The XRD and DTA–TG results expose that the YFAg–TS catalyst is a mixed phase consisting of anatase, rutile, and chlorargyrite, which is beneficial to improving the photocatalytic performance of TiO2. The SEM, TEM, and BET results disclose that the YFAg–TS film has smaller nanoparticles, higher specific surface area, and narrower pore size compared with pure TiO2 film. The XRD and TEM results exhibit that a part of yttrium can enter the TiO2 lattice to induce lattice distortion. The XPS results confirm the presence of Y3+ state in the YFAg–TS sample, and Y3+ ions can act as the trapping site of electrons to expedite the separation of electrons and holes. The UV–vis DRS results reveal that the YFAg–TS film has an obvious absorption edge shift and a narrower bandgap (2.70 eV) compared with pure TiO2 film. The PL results show that the YFAg–TS film has the highest photogenerated electrons and holes separation efficiency and charges transfer efficiency among all samples. The photocatalytic activity of the YFAg–TS was assessed by monitoring the degradation of methyl green and formaldehyde solution. The results manifest that the YFAg–TS film has high stability and excellent photocatalytic performance. The possible synergistic photocatalytic mechanism of YFAg–TS films has been discussed in this paper.

Enhanced Photocatalytic Activity of Fluorine Doped Tio2 by Loaded with Ag for Degradation of Organic Pollutants

Enhanced Photocatalytic Degradation of Organic Pollutants Under Visible Light Using Ag-Modified TiO<sub>2</sub> on Activated Carbon Fibers

Photocatalytic Degradation of Organic Dyes by a High Efficient TiO<sub>2</sub>-Based Catalysts Under Solar Light Irradiation

Enhanced photocatalytic performance of novel visible light-driven Ag–TiO 2 /SBA-15 photocatalyst

Preparation of AgI Sensitized Amorphous TiO2 As Novel High-Performance Photocatalyst for Environmental Applications

Synthesis of hollow sphere structured TiO2 loaded with Ag2O and its photocatalytic activity

Enhanced visible light photoactivity of TiO2/SnO2 films by tridoping with Y/F/Ag ions

Visible-Light-Driven Photocatalytic Activity of Ag-Loaded TiO 2 Nanoparticulate Thin Film Fabricated via PECVD-PVD Method

Synthesis, Characterization and Photocatalytic Activity of Ag-doped TiO2 Film

Preparation of F-Modified Nanosized TiO_2 and Its Methyl Orange Photodegradation Mechanism

Preparation and activity of Ag-TiO2 photocatalyst with multi-valency state

Photocatalytic degradation of methyl orange on TiO2 promoted by silver

Preparation and Characterization of TiO2 Photocatalysts by Fe3+ Doping Together with Au Deposition for the Degradation of Organic Pollutants

Synthesis of C, F Co-Doping Ag/Tio2 with Dark Catalytic Performance for Organic Dyes

Preparation of F-Modified Nanosized TiO<sub>2</sub> and Its Methyl Orange Photodegradation Mechanism

The Impact of Silver Modification on the Catalytic Activity of Iodine-Doped Titania for P-Chlorophenol Degradation under Visible-Light Irradiation

F‐doped Ag/AgBr with Enhanced Visible‐light Photocatalytic Activity and Mechanism

Fluorine Doped Anatase TiO2 with Exposed Reactive (001) Facets Supported on Porous Diatomite for Enhanced Visible-Light Photocatalytic Activity

Ag@Agx(X=Cl, Br, I) Modified N, F Codoped Tio2 Nanotubes As Effective Photocatalyst

Visible Light Induced Photodegradation of Organic Pollutants on Nitrogen and Fluorine Co-Doped TiO2 Photocatalyst.

Enhanced Visible-Light Photocatalysis Activity of TiO2/Ag Nanocomposites Prepared by the Ultrasound-Assisted Sol–Gel Method: Characterization and Degradation–Mineralization of Cationic and Anionic Dyes