Enhanced visible light photocatalytic VOC oxidation via Ag-loaded TiO2/SiO2 materials
Carolina de Araújo Gusmão,Priscila Hasse Palharim,Bruno Ramos,Douglas Gouvea,Orlando Rodrigues,Antonio Carlos Silva Costa Teixeira
DOI: https://doi.org/10.1007/s10853-023-09285-7
IF: 4.5
2024-01-18
Journal of Materials Science
Abstract:Ag-TiO 2 /SiO 2 materials were synthesized with 1, 3, 5, and 10 wt% Ag contents and extensively characterized by different techniques, including XRD, SEM, TEM, XPS, BET, UV–VIS, EPR, and PL spectroscopy. Subsequently, the activity of these materials in the degradation of a model volatile organic compound ( n -hexane) was compared by testing in a continuous gas–solid photoreactor. Loading with Ag induced stabilization of the brookite phase and crystal growth. TEM images showed d-spacing values corresponding to anatase and metallic silver. The specific surface area was lower in the Ag-modified catalysts, probably due to the blocking of the silica gel pores by Ag nanoparticles, whose size (~ 20 nm) was larger than the silica pores (~ 1.98 nm). SEM–EDS images showed heterogeneous distribution of Ag on the surface of the materials. XPS spectra showed bands referring to Ag + and Ag 0 3d, and Ti 4+ and Ti 3+ 2p. EPR analyses showed that silver loading of TiO 2 /SiO 2 greatly increased the occurrence of oxygen vacancies in the material. Finally, the band gap energies calculated from the UV–VIS spectra were lower in the silver-containing catalysts, dropping from 3.25 to 3.17 eV in the optimal material. Under visible light, while TiO 2 /SiO 2 showed no photoactivity, the Ag-modified materials presented satisfactory steady-state performance (46.4% n -hexane removal).
materials science, multidisciplinary