NiZnAl Layered Double Hydroxides As Photocatalyst under Solar Radiation for Photocatalytic Degradation of Orange G

Xiaorong Wang,Pingxiao Wu,Yonghong Lu,Zhujian Huang,Nengwu Zhu,Chen Lin,Zhi Dang

DOI: https://doi.org/10.1016/j.seppur.2014.05.026

IF: 8.6

2014-01-01

Separation and Purification Technology

Abstract:In this paper, well-crystallized NiZnAl layered double hydroxides (NiZnAl-LDHs) at different Zn2+/Ni2+ molar ratio (from 2 to 4) were prepared using dynamic urea hydrolysis method and further calcined at 873 K to obtain the layered NiZnAl mixed metal oxides with high photocatalytic activity. The as-synthesized catalysts were characterized by multiple techniques including XRD, FT-IR, TG-DSC, XPS, XRF, N-2 adsorption-desorption isotherms, UV-vis DRS, and SEM. Additionally, their photocatalytic properties were evaluated by degrading orange G (OG) under solar radiation, with the investigation of isothermal adsorption behavior of OG on NiZnAl-LDHs before. Several factors influencing the photocatalytic activity like Zn2+/Ni2+ molar ratio of the catalyst, catalyst dosage, initial dye concentration, and initial pH, have been studied and optimized as 3, 0.5 g L-1, 50 mg L-1 and neutral, respectively, with a maximum of 99% degradation of OG achieved within 100 min reaction. Furthermore, the kinetic study suggested that the photodecomposition process was well fitted to the Langmuir-Hinshelwood model and the mineralization of OG was confirmed by the FT-IR analysis of the catalyst after the degradation. Finally, a probable mechanism was proposed to explain the process of photocatalytic reaction. (C) 2014 Elsevier B.V. All rights reserved.