Fabrication of UO2-BeO composite pellets with superior thermal conductivity based on multi-parameter theoretical analyses
Rui Gao,Zhenliang Yang,Bingqing Li,Biaojie Yan,Liang Cheng,Yun Wang,Yi Zhong,Qiqi Huang,Zhiyi Wang,Mingfu Chu,Bin Bai,Xueyan Zhu,Pengcheng Zhang,Rui Li,Tong Liu
DOI: https://doi.org/10.1016/j.jnucmat.2020.152533
IF: 3.555
2020-12-01
Journal of Nuclear Materials
Abstract:<p>In this paper, the fabrication process of UO<sub>2</sub>-BeO composite pellets was optimized for improving the thermal conductivity based on multi-parameter theoretical analyses and experimental investigations. It was found that the density of BeO and UO<sub>2</sub>/BeO interfacial thermal resistance (ITR) are crucial parameters that affect the thermal conductivity of UO<sub>2</sub>-BeO. To effectively increase BeO density and decrease UO<sub>2</sub>/BeO ITR, the fabrication method of pressureless sintering with a spheroidizing process was proposed. Through this method, UO<sub>2</sub>-BeO composite with high thermal conductivity was obtained. 89.2% and 71.4% enhancements of the thermal conductivity over UO<sub>2</sub> were achieved at room temperature and 673 K, respectively. This enhancement is higher than all the reported results in the previous literatures that fabricated UO<sub>2</sub>-BeO using normal sintering temperatures (< 2023 K). The results of finite element modelling showed that the centerline temperatures of our fabricated pellets in the reactor decreased remarkably compared with UO<sub>2</sub> fuel, which would significantly improve the safety of the reactor.</p>
materials science, multidisciplinary,nuclear science & technology