Hollow spiny shell of porous Ni–Mn oxides: A facile synthesis route and their application as electrode in supercapacitors

houzhao wan,lin lv,lu peng,yunjun ruan,jia liu,xiao ji,ling miao,jianjun jiang

DOI: https://doi.org/10.1016/j.jpowsour.2015.03.107

IF: 9.2

2015-01-01

Journal of Power Sources

Abstract:Hollow spiny shell Ni–Mn precursors composed of one-dimensional nanoneedles were synthesized via a simple hydrothermal method without any template. The hollow Spiny shell Ni–Mn oxides are obtained under thermal treatment at different temperatures. The BET surface areas of Ni–Mn oxides reach up to 112 and 133 m2 g−1 when calcination temperatures occur at 300 and 400 °C, respectively. The electrochemical performances of as-synthesized hollow spiny shell Ni–Mn oxides gradually die down with annealing temperatures increasing. The porous hollow spiny shell Ni–Mn oxide obtained at 300 °C delivers a maximum capacitance of 1140 F g−1 at a high current density of 1 A g−1 after 1000th cycles and the specific capacitance of Ni–Mn oxide will increase with cycling times increasing. So, porous hollow spiny shell Ni–Mn oxide obtained at low annealing temperature can form a competitive electrode material for supercapacitors.