Pt@Nb-TiO2 Catalyst Membranes Fabricated by Electrospinning and Atomic Layer Deposition

Qing Du,Jianbo Wu,Hong Yang
DOI: https://doi.org/10.1021/cs400944p
IF: 12.9
2013-01-01
ACS Catalysis
Abstract:A facile method was developed to fabricate fibrous membranes of niobium-doped titania-supported platinum catalysts (Pt@Nb-TiO2) by a two-step approach. The process started with generating niobium-doped titania (Nb-TiO2) fibrous membranes by electrospinning, followed by the deposition of Pt nanoparticles (NPs) using an atomic layer deposition (ALD) technique. The area specific oxygen reduction reaction (ORR) activity of Pt@TiO2 catalyst membrane was increased by similar to 20 folds if 10 at.% of Nb was incorporated into the ceramic fibers. The area-specific activity also increased with the number of ALD cycles, because of the increase of the Pt loading in the catalysts. After post-treatment of the catalyst membrane at high temperature in H-2-containing atmosphere, the ORR activity became 0.28 mA/cm(Pt)(2) at 0.9 V (vs RHE), because of the improvement in conductivity of Nb-TiO2 fibers and better crystalinity of Pt NPs. The results of accelerated-stability test showed that the Pt@Nb-TiO2 catalyst membrane was highly stable and lost only 10% of its initial activity after 30 000 potential cycles (0.6 to 1.0 V vs RHE) under a strong acidic condition..
What problem does this paper attempt to address?