Abstract:CaSi2O2N2:Ce3+/Eu2+phosphors were successfully synthesized via the solid-state reaction method.Photoluminescence properties of Ce3+-doped,Eu2+-doped and Ce3+/Eu2+codoped samples are investigated.CaSi2O2N2:Ce3+phosphors show a broad band centered at 395 nm under 333 nm excitation.Red-shift occurs as the concentration of Ce3+increases.The molar quenching concentration of Ce3+is approximately 1%.CaSi2O2N2:Eu2+phosphors emit a single,intense,and broad emission band centered at 540 nm when excited at 397 nm.The molar quenching concentration of Eu2+is approximately1%.When excited at 333 nm,the codoped samples Ca0.99-2xSi2O2N2:xCe3+,xLi+,0.01Eu2+emit two broad bands centered at 395 nm and 540 nm,respectively.The emission of Eu2+is significantly enhanced by the increase of Ce3+.When Ca0.98-ySi2O2N2:0.01Ce3+,0.01Li+,yEu2+phosphors are excited at 333 nm,two broad bands with peaks at 395 and 540nm are observed.The former band(at 395nm)is weakened when increasing Eu2+content.However,the band at 540 nm reaches the maximum intensity for y=0.004.These suggest effective energy transfer mechanism from Ce3+to Eu2+taking place in the CaSi2O2N2 sample.The efficiency of energy transfer between Ce3+and Eu2+is calculated,and saturation value occurs when the concentration of Eu2+increases to 1%.The resonance-type energy transfer between Ce3+and Eu2+is dipole-dipole interaction mechanism.

Synthesis and Photoluminescence Properties of Tunable Emission Phosphors Ca4si2o7f2:Ce3+

Luminescence Properties And Energy Transfer Of Ce3+,Tb3+-Coactivated-Sialon Phosphors

Synthesis, crystal structure and luminescence properties of a Y4Si2O7N2:Ce3+ phosphor for near-UV white LEDs

Synthesis and luminescent properties of blue-emitting phosphors Ca2SiO2F2:Ce3+ for solid state lighting

Tunable Blue-Green-emitting Ca3Si2O4N2:Ce3+, Eu2+ Phosphor with Energy Transfer for Light-Emitting Diodes

Tunable Luminescence of Ce3+/Eu2+ Activated in Single-Phase Li2BaSiO4 Phosphor Via Energy Transfer

Luminescent Properties and Energy Transfer of Ca1.94Zn0.43Al1.25Si1.38O7:Ce3+, Eu2+ Phosphor

Luminescence and Energy-Transfer Properties of Color-Tunable Ca2Mg0.25Al1.5Si1.25O7:Ce(3+)/Eu(2+)/Tb(3+) Phosphors for Ultraviolet Light-Emitting Diodes.

Luminescence Properties and Ce3+→Tb3+ Energy Transfer of Li2SrSiO4:Ce3+ ,Tb3+ Phosphor

Photoluminescence Properties of Color-Tunable Novel Na2Ca4(PO4)2SiO4:Ce3+, Tb3+ Near Ultraviolet Convertible Phosphors

Photoluminescence Properties of Ce3+ and Ce3+–Eu2+ Energy Transfer in Ba1.3Ca0.7SiO4 Phosphors

Blue to green emission and energy transfer between Ce3+ ions in Ca15Si20O10N30

Luminescence properties of CaSi2O2N2 ∶Ce3+/Eu phosphors

Synthesis and luminescence properties of blue-emitting phosphor K 2 Ca 2 Si 2

Photo-/cathodoluminescence and energy transfer properties of novel Ce3+ singly doped and Ce3+/Tb3+ codoped NaBaScSi2O7 phosphors

Structure, Crystallographic Sites, And Tunable Luminescence Properties Of Eu2+ And Ce3+/Li+-Activated Ca1.65sr0.35sio4 Phosphors

Synthesis, Photoluminescence Properties and Energy Transfer Studies of Color-Adjustable Casrsio4:Ce3+,Li+,Mn2+ Phosphors

Luminescence properties and energy transfer of Ca 2 Mg 0.5 AlSi 1.5 O 7 :Ce 3 + , Eu 2 + phosphors for UV-excited white LEDs

Synthesis and Tunable Luminescent Properties of Eu-doped Ca2NaSiO4F – Coexistence of the Eu2+ and Eu3+ Centers

Synthesis and Luminescence Properties of Sr3–z(AlxSi1x)O5–xFx:zCe3+ Phosphors

Synthesis and Site-Selective Photoluminescence Property of Ca 8 La 2 (PO 4 ) 6 O 2 : Ce 3+