Size Dependence of Structure and Magnetic Properties of CoCr2O4 Nanoparticles Synthesized by Hydrothermal Technique

Zhaoming Tian,Changming Zhu,Junfeng Wang,Zhengcai Xia,Yong Liu,Songliu Yuan
DOI: https://doi.org/10.1016/j.jmmm.2014.10.090
IF: 3.097
2014-01-01
Journal of Magnetism and Magnetic Materials
Abstract:The size dependence of structure and magnetic behavior has been investigated on spinel chromite CoCr2O4 nanoparticles (NPs) with different particles from ~2.8 to ~19.7nm, synthesized by a hydrothermal technique. The microstructure analysis shows that the lattice parameter increases monotonically with reduced particle sizes. Compared with the bulk sample, all synthesized NPs exhibit lower Curie temperature (TC~87K) from paramagnetic (PM) to collinear short-range ferrimagnetic (FiM) state, and this PM–FiM transition is gradually degraded with decreased particle sizes and nearly vanishes for ~2.8nm NPs. No magnetic transition from short-range FiM order to long-range spiral spin structure is found at low temperatures contrast to the bulk ones. Instead, a cluster spin-glass (SG) transition appears for NPs with D≤5.4nm. The dynamic behavior of the cluster SG can be described by a power law with the spin relaxation time in the range of 10−10–10−8s and critical exponent zv′=9.9±0.6, in accordance with a three-dimensional Ising SG behavior. The glass transition temperature (Tg) decreases from 16.3K for ~5.4nm to 12.8K for ~2.8nm NPs.
What problem does this paper attempt to address?