Abstract:This study characterizes BaCo0.7Fe0.2Nb0.1O3-delta (BCFN) perovskite oxide and evaluates it as a potential cathode material for proton-conducting SOFCs with a BaZr0.2Ce0.7Y0.2O3-delta (BZCY) electrolyte. A four-probe DC conductivity measurement demonstrated that BCFN has a modest electrical conductivity of 2-15 5 cm(-1) in air with p-type semiconducting behavior. An electrical conductivity relaxation test showed that BCFN has higher D-chem and K-chem than the well-known Ba0.5Sr0.5CO0.8Fe0.2O3-delta oxide. In addition, it has relatively low thermal expansion coefficients (TECs) with values of 18.2 x 10(-6) K-1 and 14.4 x 10(-6) K-1 at temperature ranges of 30-900 degrees C and 30-500 degrees C, respectively. The phase reaction between BCFN and BZCY was investigated using powder and pellet reactions. EDX and XRD characterizations demonstrated that BCFN had lower reactivity with the BZCY electrolyte than strontium-containing perovskite oxides such as SrCo0.9Nb0.1O3-delta and Ba0.6Sr0.4Co0.9Nb0.2O3-delta. The impedance of BCFN was oxygen partial pressure dependent. Introducing water into the cathode atmosphere reduced the size of both the high-frequency and low-frequency arcs of the impedance spectra due to facilitated proton hopping. The cathode polarization resistance and overpotential at a current density of 100 mA cm(-2) were 0.850 Omega cm(-2) and 110 mV in dry air, which decreased to 0.43 Omega cm(-2) and 52 mV, respectively, in wet air (similar to 3% H2O) at 650 degrees C. A decrease in impedance was also observed with polarization time; this was possibly caused by polarization-induced microstructure optimization. A promising peak power density of similar to 585 mW cm(-2) was demonstrated by an anode-supported cell with a BCFN cathode at 700 degrees C. Copyright (C) 2011, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

Ybaco3zno7+Delta-Sm2o3 As The Cathode Material For Proton-Conducting Sofcs

YBaCo3ZnO7+δ–Sm2O3 as the cathode material for proton-conducting SOFCs

Electrochemical characterization of YBaCo 3ZnO 7+δ as a stable proton-conducting SOFCs cathode

A novel single phase cathode material for a proton-conducting SOFC

Characterization of Ba0.5Sr0.5Co0.7In0.1Fe0.2O3−δ As the Cathode Material for Proton‐conducting SOFCs

High Performance La0.5(Ba0.2Sr0.2Ca0.1)Co0.8Fe0.2O3-δ- BaZr0.1Ce0.7Y0.1Yb0.1O3-δ Composite Cathode for Proton-Conducting Solid Oxide Fuel Cells

Novel cobalt-free cathode materials BaCexFe1-xO3-δ for proton-conducting solid oxide fuel cells

A Cobalt-Free Sm0.5Sr0.5FeO3−δ–BaZr0.1Ce0.7Y0.2O3−δ Composite Cathode for Proton-Conducting Solid Oxide Fuel Cells

A Promising Cathode for Proton-Conducting Intermediate Temperature Solid Oxide Fuel Cells: Y0.8Ca0.2BaCo4O7+δ

Cobalt Free SrFe0.95Nb0.05O3−δ Cathode Material for Proton-Conducting Solid Oxide Fuel Cells with BaZr0.1Ce0.7Y0.2O3−δ Electrolyte

Fabrication of BaZr0.1Ce0.7Y0.2O3 – Δ ‐based Proton‐Conducting Solid Oxide Fuel Cells Co‐Fired at 1,150 °C

A Cobalt-Free SrFe0.9Sb0.1O3−δ Cathode Material for Proton-Conducting Solid Oxide Fuel Cells with Stable BaZr0.1Ce0.7Y0.1Yb0.1O3−δ Electrolyte

Pr doped barium cerate as the cathode material for proton-conducting SOFCs

Fabrication and performance of a proton-conducting solid oxide fuel cell based on a thin BaZr0.8Y0.2O3-δ electrolyte membrane

Preparation and Characterization of Ba0.5Sr0.5Fe0.9Ni0.1O3−δ–Sm0.2Ce0.8O1.9 Compose Cathode for Proton-Conducting Solid Oxide Fuel Cells

Characterization and Evaluation of BaCo0.7Fe0.2Nb0.1O3−δ As a Cathode for Proton-Conducting Solid Oxide Fuel Cells

Low Thermal Expansion Material Bi0·5Ba0·5FeO3-δ in Application for Proton-Conducting Ceramic Fuel Cells Cathode

Evaluation of SrSc0.175Nb0.025Co0.8O3-δ Perovskite As a Cathode for Proton-Conducting Solid Oxide Fuel Cells: the Possibility of in Situ Creating Protonic Conductivity and Electrochemical Performance

SrCo0.4Fe0.4Zr0.1Y0.1O3-δ, A New CO2 Tolerant Cathode for Proton-Conducting Solid Oxide Fuel Cells

Development of A Novel Type of Composite Cathode Material for Proton-Conducting Solid Oxide Fuel Cells

High Performance of Proton-Conducting Solid Oxide Fuel Cell with a Layered PrBaCo2O5+δ Cathode