Abstract:Nano-meter Y-2-SiO5:Eu-x, materials were synthesized by sol-gel method, and its structure, and morphology were characterized by XRD, FTIR and TEM. The influence of phase structure, calcination temperature and Eu3+ doping concentration on luminescence properties was investigated. The results show that the materials obtained at calcination temperature below 900 degrees C mainly present non-crystal state, while the materials mainly exhibit crystal state structure when calcined over 900 degrees C. The particle size increased with the calcination temperature. The particle size was 15 similar to 45 nm and 60 similar to 80 nm for amorphous and crystal forms, respectively. The excitation and emission spectra of materials are all affected by phase structure, calcination temperature and Eu3+ doping concentration. For Y2-xSiO5:Eu-x nanocrystal samples, in excitation spectra the charge transfer state (CTS) in crystal state absoption peak appeared red-shifted obviously compared with that in amorphous form, and in emission spectra the strong emission peak corresponding to D-5(0)-> F-7(2) transition was observed and its intensity increased and decreased, respectively, with the calcination temperature for amorphous samples and crystal samples, at the same time two novel sharp emissions peaks were found at longer wavelength and became stronger with particle size. The spectra with respect to the D-5(0)-> F-7(1) transition splitted into sharp triple peaks, but the emission spectra corresponding to D-5(0)-> F-7(0) transition was almost not affected by the crystal phase and the particle size. While in the crystal Y2-x,SiO5:Eu-x of 60 similar to 80 nm, the luminescence intensities of D-5(0)-> F-7(2) and D-5(0)-> F-7(1) transitions were influenced by Eu3+ doping concentration, when the Eu3+ doping concentration was at x=0.4, the luminescence intensity was the strongest.

Preparation, Characterization and Photoluminescence Properties of Sio2 and Sio2:Eu3+ Submicron Rods

Preparation and Photoluminescence Properties of Eu3+-Doped Al2O3 Films on Silicon Substrates by the Sol-gel Method

Synthesis and Luminescence Properties of Eu(III)-doped Silica Nanorods Based on the Sol–gel Process

Synthesis and Luminescence Properties of Monodisperse SiO2@SiO2:Eu3+ Microspheres

Synthesis and Properties of Core Shell Sio2@Y2o3:Eu3+ Wavelength Conversion Materials

A Facile Method for the Fabrication of Luminescent Eu3+-Doped SiO2 Nanowires

Preparation and luminescence properties of Eu2+ in SiO2 xerogels

Preparation and Optical Properties of Sulfur-Doped Silicon Oxide Microbelts and Microrods

Synthesis, Structure, and Optical Properties of Sio2:Eu3+ Nanowires

Synthesis, structure, and luminescence properties of SrSiAl<sub>2</sub>O<sub>3</sub>N<sub>2</sub>:Eu<sup>2+</sup> phosphors for light-emitting devices and field emission displays

In Situ Sol–gel Composition of Multicomponent Hybrid Precursors to Luminescent Novel Unexpected Microrod of Y2SiO5:Eu3+ Employing Different Silicate Sources

Sol-Gel Preparation and Luminescent Properties of Eu3+ Doped Al2O3 Hollow Microspheres

Facile Synthesis and Luminescence Properties of Silica Submicron Rods

Synthesis and Luminescent Properties of Monodisperse Core–shell Structured SiO2@Lu2O3:Eu3+ Microspheres

Luminescent Properties and Energy Transfer of Gd3+/Eu3+ Co-Doped High Uniform Meso-Silica Nanorods

The Synthesis And Luminescence Properties Of Lu2o3:Eu3+ Rods And Its Comparative Analysis With Lu2o2s:Eu3+ Rods

Synthesis, Luminescent and Drug-Release Properties of Sio2@Y2o3:Eu Hollow Mesoporous Microspheres

Synthesis and Characterization of Sio2/Gd2o3 : Eu Core-Shell Luminescent Materials

Synthesis, Structure, and Optical Properties of SiO 2 :Eu 3+ Nanowires

Nano Y2-xSiO5:Eux3+: Preparation, Structure Effect on Emitting Properties,Emitting Mechanism

Preparation and Luminescence of Nano-Sized In2O3and Rare-Earth Co-Doped SiO2thin Films