Microstructure Evolution and Mechanical Properties of Near-Α Ti-8Al-1Mo-1V Alloy at Different Solution Temperatures and Cooling Rates
Xiaohui Shi,Weidong Zeng,Yu Long,Yanchun Zhu
DOI: https://doi.org/10.1016/j.jallcom.2017.08.165
IF: 6.2
2017-01-01
Journal of Alloys and Compounds
Abstract:Nine solution-ageing treatments with different solution temperatures (915 degrees C, 960 degrees C, 1010 degrees C) and cooling media (water quenching, oil cooling, air cooling) were firstly conducted on the rolled near-alpha Ti8Al-1Mo-1V alloy. The microstructure evolution behavior and various mechanical properties of this alloy were studied. The results show that solution temperature can greatly influence microstructure features. By increasing solution temperature, the volume fraction of primary alpha phase continuously decreased, the original shapeless primary a phase was sectioned and gradually showed equiaxed shape, and the beta grain kept growing until its grain boundary reached the biggest sectional area of primary alpha particles (pinning effect). Due to the proper mixture of primary alpha and lamellar alpha phase, Ti-8Al-1Mo-1V alloy can achieve the best combination of tensile properties, thermal exposure properties and creep properties after being solution-treated at 1010 degrees C followed by oil cooling. Based on above results, high solution temperature is necessary to the application of Ti-8Al-1Mo-1V alloy. Thus a comprehensive study on the microstructure evolution behavior of Ti-8Al-1Mo-1V alloy at various precisely controlled cooling rates on cooling down from 1010 degrees C is of great significance. The results show that: with decreasing cooling rate on cooling down from 1010 degrees C, the volume fraction and the diameter of equiaxed alpha as well as the thicknesses of the grain boundary alpha and the lamellar alpha continuously increased. Equiaxed alpha shows an evolution process of precipitation, growth, mergence of adjacent equiaxed alpha and mergence between equiaxed alpha and lamellar alpha. Obvious changes of equiaxed alpha only happened at the cooling rates below 15 degrees C/s. However, for grain boundary alpha and lamellar alpha, the mutant range is "below 40 degrees C/s". The exponential decay formula perform well in quantitatively characterizing the microstructure features-cooling rate relations. (C) 2017 Elsevier B.V. All rights reserved.