Coercivity enhancement of a Nd–Fe–B sintered magnet by diffusion of Nd 70 Cu 30 alloy under pressure

fugang chen,tieqiao zhang,jing wang,lanting zhang,gaofeng zhou

DOI: https://doi.org/10.1016/j.scriptamat.2015.05.015

IF: 6.302

2015-01-01

Scripta Materialia

Abstract:Application of pressure during grain boundary diffusion process (GBDP) using Nd70Cu30 eutectic alloy enhances the coercivity greatly from 1367kA/m in the annealed state to 1660kA/m. The uniformity of coercivity distribution was improved due to the large effective diffusion depth under pressure. Continuous grain boundary phase was observed both on the surface and in the center of the magnet after GBDP under pressure. Mechanism of coercivity enhancement due to micro cracks is discussed based on the observation.