Cellulose Membranes from Cellulose CO 2 -Based Reversible Ionic Liquid Solutions
Yuanlong Guo,Long Cai,Gu Guo,Haibo Xie,Lihua Zhang,Longming Jin,Songmiao Liang,Lijie Hu,Qinqin Xu,Qiang Zheng
DOI: https://doi.org/10.1021/acssuschemeng.1c03609
2021-08-19
Abstract:Regenerated cellulose membranes (RCMs) were prepared from cellulose sufficiently dissolved in [TMGH]2+[OOCOCH2CH2OCOO]2–/DMSO (XILS = 0.2, XILs is the mole fraction of reversible ionic liquids in the mixed solvents) mixed solution under mild conditions (50 °C, 3 h, PCO2 = 0.2 MPa) using different coagulation baths of ethanol, methanol, NaOH, and H2SO4 aqueous solutions. The structure and properties of these membranes were characterized using various characteristic technologies. The membrane regenerated from ethanol exhibited good thermostability and mechanical, water vapor, and oxygen barrier properties with a tensile strength of 56.2 MPa, a tensile strain of 20.4%, an excellent water vapor permeability of 8.7 × 10–3 g μm/m2 day kPa, and an oxygen permeability (OP) of 4.087 cm3 μm/m2 day atm. The membranes regenerated from aqueous solutions of alkali and acid have an OP that tends to zero. This study provides a novel dissolving strategy to prepare cellulose membranes that have potential applications in the packaging, food, and agricultural industries.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c03609.EDS results of RCMs from different regeneration baths and water contact angles of RCMs (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology