Abstract:We examine the contribution of crack bridging and surface elasticity to the elastic interaction between a mode III finite crack and a screw dislocation. The surface effect on the crack faces is incorporated by using the continuum-based surface/interface model of Gurtin and Murdoch. The crack faces are subjected to a bridging force which is assumed to be proportional to the crack opening displacement, whereas the bridging stiffness is allowed to vary arbitrarily along the crack. By considering a continuous distribution of both screw dislocations and line forces on the crack, the boundary value problem is reduced to two decoupled first-order Cauchy singular integro-differential equations. After the expansion of the unknown line dislocation and line force densities and the known variable bridging stiffness into Chebyshev polynomials, these singular integro-differential equations are solved numerically using the collocation method. Owing to the incorporation of surface elasticity, the stresses at the crack tips only exhibit the weak logarithmic singularity when the dislocation is located on the real axis where the crack is located, whereas in the case when the dislocation is not on the real axis, the stresses at the crack tips exhibit both the weak logarithmic and the strong square-root singularities. The two densities, the crack opening displacement across the crack faces and the image force acting on the screw dislocation are specifically calculated. We note that crack bridging only exerts an effect on the line dislocation density but has no influence on the line force density. In addition, we demonstrate that both surface elasticity and crack bridging can reduce the strengths of the logarithmic stress singularity at the crack tips and the magnitude of the crack opening displacement across the crack faces. Our results also clearly show that both crack bridging and surface elasticity exert a significant influence on the magnitude and direction of the image force acting on the screw dislocation.

Fracture Behavior Investigation For A Pileup Of Edge Dislocations Interacting With A Nanoscale Inhomogeneity With Interface Effects

Influence of Nanoscale Inhomogeneity Incorporating Interface Effect on Crack Nucleation at Intersection of Twin and Grain Boundary in Nanocomposite

Monte Carlo Simulation of Complex 2D Cohesive Fracture in Random Heterogeneous Quasi-Brittle Materials

Monte Carlo simulation of complex cohesive fracture in random heterogeneous quasi-brittle materials

Progress in Complex 2d and 3d Cohesive Fracture Modelling Considering Random Heterogeneity

Monte Carlo Simulation of Complex Cohesive Fracture in Random Heterogeneous Quasi-Brittle Materials: A 3D Study

An atomistic-to-microscale computational analysis of the dislocation pileup-induced local stresses near an interface in plastically deformed two-phase materials

Interaction Between an Edge Dislocation and a Bridged Crack with Surface Elasticity

Effects of Surface Elasticity on Mixed-Mode Fracture

Interfacial crack-tip field in anisotropic elastic solids

Nanomechanics and Nanocomposites: Mechanical Behaviors

How Are Microstructural Defect Interactions Linked to Simultaneous Intergranular and Transgranular Fracture Modes in Polycrystalline Systems?

Finite size effects on crack front pinning at heterogeneous planar interfaces: Experimental, finite elements and perturbation approaches

Mechanics of dynamic debonding

Intergranular fracture, grain-boundary structure, and dislocation-density interactions in FCC bicrystals

Effects of infilling materials on mechanical behaviors and cracking process of pre-cracked rock: Insights from a hybrid continuum-discontinuum method

Influence of Dislocation Pile-Up on Main Crack Propagation in Nanocrystals in the Hydrogen Environment

Interface Stress Around a Nanosized Spherical Inhomogeneity under Asymmetric Dynamic Loads

Plastic Mismatch Effect on Plasticity Induced Crack Closure: Fatigue Crack Propagation Perpendicularly Across a Plastically Mismatched Interface

Study of the effects of geometrically necessary dislocations and boundary conditions on size effects in a higher-order crystal plasticity model

Interaction of an interfacial crack with linear micro-defects under out-of-plane shear loading