The Role of Transition Metal Doping in Enhancing Hydrogen Storage Capacity in Porous Carbon Materials
Xue Gao,Zeming Zhong,Liangjun Huang,Yuchen Mao,Hui Wang,Jiangwen Liu,Liuzhang Ouyang,Lei Zhang,Mengjiao Han,Xiuliang Ma,Min Zhu
DOI: https://doi.org/10.1016/j.nanoen.2023.109038
IF: 17.6
2023-10-28
Nano Energy
Abstract:Porous carbon materials with high specific surface area are potential hydrogen storage materials. However, due to the weak van der Waals forces between the material and H 2 , hydrogen can generally be stored only at a cryogenic temperature under high hydrogen pressure. To solve this problem, in this work, ZIF-8-derived porous carbon material (PCM) modified with transition metals (PCM-TMs, TM: Mn, Fe, Ni) was prepared to investigate the role of TM doping. The developed PCM-TMs have a high specific surface area (up to 1363 m 2 /g) and pore volume (up to 0.89 cm 3 /g). Experimental results show that PCM-TMs exhibit higher hydrogen storage capacity, usable capacity, and hydrogen uptake capacity per specific surface area compared to PCM. In addition, PCM-TMs have a higher isosteric heat of adsorption (Q st ) than PCM, which suggests that TM doping enhances the interaction between H 2 and carbon materials. Theoretical calculations further indicate that this interaction is a nearly weak chemisorption force (~9.27 kJ/mol). Notably, Mn-doped porous carbon material (PCM-Mn) exhibits a hydrogen storage capacity of ~3.45 wt.% (20.44 g/L) at 77 K under 35 bar-H 2 . Even at 253 K under 50 bar-H 2 , the capacity can reach ~1.41 wt.% (8.34 g/L). The hydrogen uptake capacity per specific surface area for PCM-Mn reaches 1.03×10 -3 wt.% / m 2 ·g -1 at 253 K under 50 bar-H 2 , which is 1.5 times larger than that of PCM. Under proper operating conditions, such as loading at 77 K and 35 bar-H 2 , and discharging at 253 K and 2 bar-H 2 , PCM-Mn can achieve a usable capacity of at least 19.30 g/L. The hydrogenation kinetics curves reveal that PCM-Mn can store 1.39 wt.%-H 2 (8.25 g/L) under 12 MPa H 2 at 298 K, while it is only 0.88 wt.% (5.53 g/L) for PCM at the same condition. This work provides valuable insight into improving the hydrogen storage performance of hydrogen storage materials of physisorption.
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology