Hierarchical Porous Li 2 Mg(NH) 2 @C Nanowires with Long Cycle Life Towards Stable Hydrogen Storage

Guanglin Xia,Yingbin Tan,Dan Li,Zaiping Guo,Huakun Liu,Zongwen Liu,Xuebin Yu

DOI: https://doi.org/10.1038/srep06599

IF: 4.6

2014-01-01

Scientific Reports

Abstract:The hierarchical porous Li 2 Mg(NH) 2 @C nanowires full of micropores, mesopores and macropores are successfully fabricated via a single-nozzle electrospinning technique combined with in-situ reaction between the precursors, i.e., MgCl 2 and LiN 3 , under physical restriction upon thermal annealing. The explosive decomposition of LiN 3 well dispersed in the electrospun nanowires during carbothermal treatment induces a highly porous structure, which provides a favourable way for H 2 delivering in and out of Li 2 Mg(NH) 2 nanoparticles simultaneously realized by the space-confinement of the porous carbon coating. As a result, the thus-fabricated Li 2 Mg(NH) 2 @C nanowires present significantly enhanced thermodynamics and kinetics towards hydrogen storage performance, e.g., a complete cycle of H 2 uptake and release with a capacity close to the theoretical value at a temperature as low as 105°C. This is, to the best of our knowledge, the lowest cycling temperature reported to date. More interestingly, induced by the nanosize effects and space-confinement function of porous carbon coating, a excellently stable regeneration without apparent degradation after 20 de-/re-hydrogenation cycles at a temperature as low as 130°C was achieved for the as-prepared Li 2 Mg(NH) 2 @C nanowires.