Abstract:Flawless porous fibrous alumina ceramics with high performance were fabricated via a novel approach involving direct coagulation casting and lost-mold method. Stable alumina suspensions were prepared by adding sodium tri-polyphosphate as dispersant using alumina fibers as raw material and K2SO4 as sintering aid. Resin-coated sand molds with designed shapes for suspension casting were fabricated through 3D printing with subsequent post-treatments. Alumina green bodies were obtained by in situ coagulation of the suspension after treating at 90 degrees C within 40 minutes. Porous alumina ceramics were obtained after direct furnace sintering of green bodies without demolding, in which the molds would collapse automatically at around 650 degrees C with less exhaust emission. The effect of various K2SO4 contents and sintering temperatures on mechanical properties of porous ceramics was investigated. The SEM results showed that the fibers interconnected with obvious interfacial bondings on junctions when sintered at 1450 degrees C. The XRD patterns showed that the sample sintered with various K2SO4 additions consisted of different phases, mainly including aluminosilicates. Porosity of ceramic samples increased slightly whereas the compressive strength enhanced significantly with increasing K2SO4 addition. The density of sintered samples with different K2SO4 contents was in accord with the porosity variation tendency. The ceramic samples had uniform pore size distribution with average size from 3.18 to 7.24 m as increasing K2SO4 addition to 40 wt%. This approach may provide a convenient and general route to fabricate various dense and porous advanced ceramics with complex shapes and good composition homogeneity.

The Role of CuO–TiO 2 Additives in the Preparation of High-Strength Porous Alumina Scaffolds Using Directional Freeze Casting

Effects of Composition and Sintering Temperature on the Structure and Compressive Property of the Lamellar Al2O3–ZrO2 Scaffolds Prepared by Freeze Casting

Fabrication and Characterization of Robust Freeze-Cast Alumina Scaffolds with Dense Ceramic Walls and Controllable Pore Sizes

Preparation of High-Strength Al–Mg–Si/Al 2 O 3 Composites with Lamellar Structures Using Freeze Casting and Pressureless Infiltration Techniques

Effects of Oxide Addition on the Microstructure and Mechanical Properties of Lamellar SiC Scaffolds and Al–Si–Mg/SiC Composites Prepared by Freeze Casting and Pressureless Infiltration

Preparation of Porous Ceramic Materials by Alumina Fiber Framework

Fabrication of Porous Fibrous Alumina Ceramics by Direct Coagulation Casting Combined with 3D Printing

Simultaneous control of mechanical strength and hierarchical structure in freeze‐casted porous alumina by two‐step sintering

Microstructures and Properties of Porous TiAl-based Intermetallics Prepared by Freeze-Casting

Fabrication and compressive properties of directional porous titanium scaffold by freeze casting TiH2 powders

The controllable microstructure of porous Al2O3 ceramics prepared via a novel freeze casting route

Microstructure, Phase Compositions and in Vitro Evaluation of Freeze Casting Hydroxyapatite-Silica Scaffolds

Improvement of pore orientation and mechanical properties for hydroxyapatite – alumina composite porous scaffolds

Fabrication of Porous Alumina Ceramics with Directional Pore Channels Structure by Freeze-Gel Casting Processing

Pore Structures and Mechanical Properties of Porous Titanium Scaffolds by Bidirectional Freeze Casting.

Porous Al2o3 Prepared Via Freeze Casting And Its Biocompatibility

Porous Al2O3 Ceramics with Spontaneously Formed Pores and Enhanced Strength Prepared by Indirect Selective Laser Sintering Combined with Reaction Bonding

Effect of K2SO4 additions on properties of porous fibrous alumina ceramics prepared by DCC and lost‐mold method

Microstructures and High-Temperature Strength of Gel-Casting Al2O3-based Ceramic Molds with Coated Aluminum Additive

Synthesis of Porous α-Al_2O_3 Ceramics by Freeze-Casting Processing

Effects of Composite Sintering Additives: Al(OH)3+Y2O3+CaF2 on the Performance of Porous Mullite Oxide-Bonded SiC Ceramics