Growth and Crystallization of Calcium Phosohate Mediated by Bombyx Mori Silk Fibrion
Jia-jia Zhong,Zheng-zhong Shao
DOI: https://doi.org/10.11777/j.issn1000-3304.2014.14155
2014-01-01
Acta Polymerica Sinica
Abstract:Amorphous calcium phosphate (ACP) has excellent biocompatibility,, osteoconduction and biodegradability. However, as it can be transformed easily to a more thermal stable phase, i. e. HAP, ACP shows poor stability in solution. As a soluble and biocompatible additive, regenerated silk fibroin (RSF) can mediate the growth of inorganic crystals. If the RSF is capable of inducing and stabilizing of the ACP, it will be desirable to expand its application to the field of bone repair. The pH value of the mineralization solution increased slowly when the ammonia gas diffused into the solution, leading to the precipitation of calcium phosphate. The morphology and polymorph of calcium phosphates were characterized by SEM, TEM, SAED, XRD and FTIR. Generally, the spherical particles were ACP and the aggregated sheets were HAP in our work. The results also showed that ACP could be obtained by adjusting the mineralization time, the weight concentration of RSF, the molar concentrations of calcium ion and phosphate ion. When the RSF and Ca2+/PO43- concentrations were fixed to 0.5% and 2 mmol/L, respectively, only ACP could be obtained after 1 h; however, both ACP and HAP could be produced when the duration of mineralization was increased to 3 h. Moreover, all the ACP would be transformed to HAP when the time was increased to 24 h. On the other side, when the Ca2+/PO43- concentrations increased, a higher RSF concentration would be needed to induce the growth of ACP. For example, ACP could be produced under a certain condition that the mineralization time and the RSF concentration were 1 h and 1% respectively, supplemental with 3 mmol/L Ca2+/PO43- concentrations, but ACP couldn't be obtained at any concentration of RSF when the ion concentration was reached to 5 mmol/L. Furthermore, it was found that RSF with higher molecular weight could induce the growth of ACP in a lower concentration under the same condition. The stable ACP/RSF hybrid may have the great potential in the bone repairing.