Formation of Hierarchical Bone-Like Apatites on Silk Microfiber Templates Via Biomineralization

Zongpu Xu,Liyang Shi,Doudou Hu,Binhui Hu,Mingying Yang,Liangjun Zhu

DOI: https://doi.org/10.1039/c6ra17199k

IF: 4.036

2016-01-01

RSC Advances

Abstract:Hierarchical bone-like apatites can be formed on silk microfiber templates and the resulting biocomposites achieved good cytocompatibility.

What problem does this paper attempt to address?

Characterization and Cytocompatibility of Premineralized Silk Fibroin/Chitosan Composite Scaffolds

施李杨,邓连霞,杨明英,张海萍,Mandal Namita,朱良均

DOI: https://doi.org/10.16865/j.cnki.1000-7555.2013.11.010

2013-01-01

Abstract:Silk fibroin/chitosan scaffolds were prepared through lyophilization, then hydroxyapatite was deposited by premineralization to obtain porous hydroxyapatite (HA)-silk fibroin/chitosan composite scaffolds.Composite scaffolds were characterized by Fourier transform infrared analysis (FT-IR), X-ray diffraction (XRD), scanning electronic microscopy (SEM), thermogravimetry analysis (TGA), compressive modulus and porosity, as well as the proliferation of MG-63 cells on composite scaffolds was detected by WST-1 method. The results reveal that the structure of deposited HA is a weak crystallinity, which deposits on the wall of pore. With the increase of premineralization cycles, the amount of HA and compressive modulus of premineralized composite scaffolds are significantly increased, the porosity keeps about 90%. WST-1 assay shows that premineralized composite scaffolds deposited with HA dramatically enhance the proliferation of cells, and possess a great cytocompatibility.
Effects of Different Structure Silk Fibroin on Crystallization of Hydroxyapatite

FENG Qiang,MIN Si-Jia,ZHANG Hai-Ping,GAO Xin,WANG Qi-Chong,ZHU Liang-Jun

DOI: https://doi.org/10.3969/j.issn.0257-4799.2008.03.015

2008-01-01

Abstract:In this paper,we investigated the effect of different structure silk fibroin on crystallization of hydroxyapatite(HA),so as to provide the evidences for HA/silk fibroin composite used as a scaffold in the bone tissue engineering.A kind of silk fibroin(SF) with coil/helical structure was prepared through neutral salt dissolution method,and the other kind of silk fibroin(ALSF) with β-sheet structure was obtained from the former SF by treatment of alcohol solution.HA/SF and HA/ALSF composites were respectively deposited with the organic template of those two silk fibroin.The second structure,phase composition and morphology of HA,HA/SF and HA/ALSF composites were investigated by Fourier transform infrared spectroscopy(FTIR),X-ray diffraction(XRD) and transmission electron microscopy(TEM).These results showed that nucleation and growth of HA were affected by silk fibroin structure,which induced different morphology and particle size of HA.
Air-plasma Treatment Promotes Bone-Like Nano-Hydroxylapatite Formation on Protein Films for Enhanced in Vivo Osteogenesis

Qing Zhang,Lu Ma,Shengnan Zheng,Yaru Wang,Meilin Feng,Yajun Shuai,Bo Duan,Xin Fan,Mingying Yang,Chuanbin Mao

DOI: https://doi.org/10.1039/c9bm00020h

2019-01-01

Biomaterials Science

Abstract:Introducing hydroxylapatite (HAp) into biomolecular materials is a promising approach to improve their bone regenerative capability. Thus a facile method needs to be developed to achieve this goal. Here we show that a simple air-plasma treatment of silk fibroin (SF) films for 5 min induced the formation of bone-like plate-shaped nano-HAp (nHAp) on their surface and the resultant material efficiently enhanced in vivo osteogenesis. The air-plasma-treated SF films (termed A-SF) presented surface nano-pillars and enhanced hydrophilicity compared to the pristine SF films (termed SF), making the A-SF and SF films induce the formation of plate-shaped/more-crystalline and needle-like/less-crystalline nHAp, respectively. The mineralized A-SF and SF films (termed A-SF-nHAp and SF-nHAp, respectively) and their non-mineralized counterparts were seeded with rat mesenchymal stem cells and subcutaneously implanted into the rat models. The A-SF-nHAp and A-SF films exhibited more efficient bone formation than the SFnHAp and SF films in 4 weeks due to their unique nanotopography, with the A-SF-nHAp films being more efficient than the A-SF films. This work shows that a combination of the air-plasma treatment and the subsequent nHAp mineralization most efficiently promotes bone formation. Our plasma-based method is an attractive approach to enhance the bone regenerative capacity of protein-based biomaterials.
Mineralization and Biocompatibility of Antheraea Pernyi (A. Pernyi) Silk Sericin Film for Potential Bone Tissue Engineering

Mingying Yang,N. P. Mandal,Yajun Shuai,Guanshan Zhou,Sijia Min,Liang Zhu

DOI: https://doi.org/10.3233/bme-130873

2014-01-01

Bio-Medical Materials and Engineering

Abstract:This study aimed to investigate the mineralization of Antheraea pernyi (A. pernyi) silk sericin. Mineralization of A. pernyi sericin was performed by alternative soaking in calcium and phosphate. The inhibition of precipitation of calcium carbonate and von Kossa staining on A. pernyi sericin were tested, and the corresponding results prove that A. pernyi sericin has Ca binding activity. Scanning electron microscope (SEM) observation shows that spherical crystals could be nucleated on the A. pernyi sericin film. These crystals were confirmed to be hydroxyapatite according to FT-IR and XRD spectra, indicating that A. pernyi sericin is capable of mineralization. In addition, cell adhesion and growth activity assay demonstrate that A. pernyi sericin shows excellent biocompatibility for the growth of MG-63 cells.
Antheraea pernyi silk sericin mediating biomimetic nucleation and growth of hydroxylapatite crystals promoting bone matrix formation.

Zhuang Jiayao,Zhou Guanshan,Zhang Jinchi,Chen Yuyin,Zhu Yongqiang

DOI: https://doi.org/10.1002/jemt.22793

2017-01-01

Microscopy Research and Technique

Abstract:Bone biomineralization is well-regulated processes mediated by extracellular matrix proteins. The materials that can direct nucleation of hydroxylapatite (HAp) crystals and assembly of well-structure dmaterial-minerals complex are the key to mimicking the natural mineralization. This study used sericin from Antheraea pernyi (A.pernyi), non-mulberry silkworm cocoon as template to mediate nucleation of HAp crystals. Here we find out that AS (Antheraea pernyi sericin) can nucleate the formation HAp crystals in simulated body fluid verified by XRD and FTIR observations. The HAp crystals are organized into nano-rods oriented with c-axis preferentially parallel to the long axis of AS due to hydrogen bonds and electrostatic interaction and finally aggregated into HAp globule. The cell culture of human bone marrow-derived mesenchymal stem cells (BMSCs) showed that the HAp crystals mediated by AS not only stimulate cell adhesion and proliferation but also promote of osteogenic differentiation, suggesting that the resultant mineralized AS biomaterial has potential in promoting bone formation. Thus our work will provide significant implication on biomineralization of A. pernyi silk sericin as a potential scaffold for tissue engineering.
Growth Of Hydroxyapatite Crystals On Bombyx Mori (B. Mori) Silk Fibroin

Yajun Shuai,Guanshan Zhou,Namita Mandal,Sijia Min,Liang Zhu,Mingying Yang

DOI: https://doi.org/10.4028/www.scientific.net/AMR.796.43

2013-01-01

Abstract:As a natural protein polymer, Bombyx mori silk fibroin (SF) has superior characteristics such as excellent mechanical properties, biocompatibility and biodegradation which make SF to be a potential candidate in the field of biomaterials. It has been reported that the mineralized SF can be used for bone repair and regeneration in the bone tissue engineering. In order to map out the growth process of hydroxyapatite (HAp) induced by SF in the mineralized buffer solution, the co-solution of SF and supersaturated simulated body fluid (1.5 SBF) was incubated at 37.2 degrees C for 7 days and observed by using TEM, DSC, DTA and TGA in this study. The TEM results indicated that nanoscale crystal nuclei were found along the surface of SF in the initial stage of mineralization and finally these crystals aggregated into three-dimensional network. DSC and DTA results showed that the thermal stability of HAp/SF was greatly improved by increasing incubation duration and that the phase transition of HAp occurred from metastable state to steady state. TGA results suggested the organic content of HAp/SF complex was about 21% which was similar to the natural bone.
Biomineralization of Natural Collagenous Nanofibrous Membranes and Their Potential Use in Bone Tissue Engineering.

Yang Mingying,Zhou Guanshan,Castano-Izquierdo Harold,Zhu Ye,Mao Chuanbin

DOI: https://doi.org/10.1166/jbn.2015.2038

2015-01-01

Journal of Biomedical Nanotechnology

Abstract:Small intestinal submucosa (SIS) membranes as a decellularized tissue are known to be a natural nanofibrous biomaterial mainly made of type I collagen fibers and containing some growth factors (fibroblast growth factor 2 and transforming growth factor beta) desired in tissue engineering. Here we show that the SIS membranes can promote the formation of bone mineral hydroxylapatite (HAP) crystals along the collagen fibers constituting the membranes from a HAP-supersaturated solution. The resultant biomineralized HAP-SIS scaffolds were found to promote the attachment, growth and osteogenic differentiation of mesenchymal stem cells (MSCs) in both basal and osteogenic media by the evaluation of osteogenic marker formation. More importantly, the HAP-SIS scaffolds could induce the osteogenic differentiation in the basal media without osteogenic supplements due to the presence of HAP crystals in the scaffolds. Histological characterization of the MSC-seeded scaffolds showed that HAP-SIS scaffolds are biocompatible and promote the formation of new tissue in vitro. The biomineralized SIS membranes mimic some aspects of natural bone in terms of the composition and nanostructures and can find potential use in bone tissue engineering.
Nucleation of Hydroxyapatite on Antheraea Pernyi (A. Pernyi) Silk Fibroin Film

Mingying Yang,Yajun Shuai,Guanshan Zhou,Namita Mandal,Liangjun Zhu

DOI: https://doi.org/10.3233/bme-130861

2014-01-01

Bio-Medical Materials and Engineering

Abstract:Antheraea pernyi (A. pernyi) silk fibroin, which is spun from a wild silkworm, has increasingly attracted interest in the field of tissue engineering. The aim of this study was to investigate the nucleation of hydroxyapatite (HAp) on A. pernyi fibroin film. Von Kossa staining proved that A. pernyi fibroin had Ca binding activity. The A. pernyi fibroin film was mineralized with HAp crystals by alternative soaking in calcium and phosphate solutions. Spherical crystals were nucleated on the A. pernyi fibroin film according to scanning electron microscopeimaging results. The FT-IR and X-ray diffraction spectra confirmed that these spherical crystals were HAp. The results of in vitro cell culture using MG-63 cells demonstrated that the mineralized A. pernyi fibroin film showed excellent cytocompatibility and sound improvement of the MG-63 cellviability.
Silk as templates for hydroxyapatite biomineralization: A comparative study of Bombyx mori and Antheraea pernyi silkworm silks

Huijie Zhang,Renchuan You,Kun Yan,Zhentan Lu,Qunmei Fan,Xiufang Li,Dong Wang

DOI: https://doi.org/10.1016/j.ijbiomac.2020.08.142

IF: 8.2

2020-12-01

International Journal of Biological Macromolecules

Abstract:Silk is extensively investigated in bone tissue engineering due to its extraordinary mechanical properties and ability to regulate biomineralization. Protein templates regulate biomineralization process through chemical interaction with ions. However, the effect of structural differences in silk fibroin on biomineralization has not been studied in detail. In this study, Antheraea pernyi silk fibroin (ASF) and Bombyx mori silk fibroin (BSF) fibers were used as templates to study the effect of silk species on biomineralization. The results showed that silk fibroin could induce the formation of calcium-deficient hydroxyapatite in simulated body fluid (SBF), and the SBF treatment resulted in the formation of silk I crystals. Compared with BSF, ASF exhibited a higher ability to induce mineralization, which may depend on the differences in hydrophilic amorphous fractions between ASF and BSF. The amorphous fractions of ASF contain more acidic amino acids, which can provide more nucleation sites in the initial stage of mineralization, resulting in faster mineralization process and more mineral deposits. This study decodes the key role of silk fibroin fractions on biomineralization, and provides deeper insights for the study of silk fibroin as biomineralization template and bone repair materials.

polymer science,biochemistry & molecular biology,chemistry, applied
Silk Protein-Mediated Biomineralization: From Bioinspired Strategies and Advanced Functions to Biomedical Applications

Lantian Ma,Yuxu Sun,Qichao Cheng,Zhangze Yang,Jie Wang,Zongpu Xu,Mingying Yang,Yajun Shuai

DOI: https://doi.org/10.1021/acsami.3c04067

IF: 9.5

2023-07-08

ACS Applied Materials & Interfaces

Abstract:Biomineralization refers to the process through which minerals nucleate in a structured manner to form specific crystal structures by the regulating of biomacromolecules. Biomineralization occurs in bones and teeth within the human body, where collagen acts as a template for the nucleation of hydroxyapatite (HA) crystals. Similar to collagen, silk proteins spun by silkworms can also serve as templates for the nucleation and growth of inorganic substances at interfaces. By enabling the binding of...

materials science, multidisciplinary,nanoscience & nanotechnology
Biomimetic Synthesis and Biocompatibility Evaluation of Carbonated Apatites Template-Mediated by Heparin.

Yi Deng,Yuhua Sun,Xiaofang Chen,Peizhi Zhu,Shicheng Wei

DOI: https://doi.org/10.1016/j.msec.2013.03.016

2013-01-01

Materials Science and Engineering C

Abstract:Biomimetic synthesis of carbonated apatites with good biocompatibility is a promising strategy for the broadening application of apatites for bone tissue engineering. Most researchers were interested in collagen or gelatin-based templates for synthesis of apatite minerals. Inspired by recent findings about the important role of polysaccharides in bone biomineralization, here we reported that heparin, a mucopolysaccharide, was used to synthesize carbonated apatites in vitro. The results indicated that the Ca/P ratio, carbon content, crystallinity and morphology of the apatites varied depending on the heparin concentration and the initial pH value. The morphology of apatite changed from flake-shaped to needle-shaped, and the degree of crystallinity decreased with the increasing of heparin concentration. Biocompatibility of the apatites was tested by proliferation and alkaline phosphatase activity of MC3T3-E1 cells. The results suggested that carbonated apatites synthesized in the presence of heparin were more favorable to the proliferation and differentiation of MC3T3-E1 cells compared with traditional method. In summary, the heparin concentration and the initial pH value play a key role in the chemical constitution and morphology, as well as biological properties of apatites. These biocompatible nano-apatite crystals hold great potential to be applied as bioactive materials for bone tissue engineering.
In Vitro Growth of Bioactive Nanostructured Apatites Via Agar-Gelatin Hybrid Hydrogel.

Yi Deng,Xianghui Zhao,Yongsheng Zhou,Peizhi Zhu,Li Zhang,Shicheng Wei

DOI: https://doi.org/10.1166/jbn.2013.1707

2013-01-01

Journal of Biomedical Nanotechnology

Abstract:Biomimetic synthesis of bone-like carbonated apatite with good biocompatibility is a promising strategy for the development of novel biomaterials for bone engineering applications. Most research efforts have been focused on only protein-based or only polysaccharide-based template for synthesis of apatite minerals. To understand the cooperative roles of gelatin and polysaccharide playing in the biomineralization, agar hydrogel, gelatin and agar-gelatin hybrid hydrogel were respectively introduced as mineralization matrix for the in vitro growth of apatite in the study. It was shown that bundle-like carbonated apatite was successfully prepared in agar-gelatin hybrid hydrogel for the first time, through the interaction between apatite and matrix macromolecule under physiological temperature. Moreover, the in vitro biocompatibility of the prepared nanostructured apatite crystals was investigated using CCK-8 assay and alkaline phosphatase activity of osteoblast-like MC3T3-E1. Compared with HA synthesized by traditional method, the obtained apatite in agar-gelatin hybrid hydrogel could provide significantly higher cell viability and alkaline phosphatase activity. Through the study, we could better understand the role of gelatin and polysaccharide in bone formation process, and the product is a promising candidate to be used in bone tissue engineering.
A Novel Nanocomposite Particle of Hydroxyapatite and Silk Fibroin: Biomimetic Synthesis and Its Biocompatibility

Lin Niu,Rui Zou,Qida Liu,Quanli Li,Xinmin Chen,Zhiqing Chen

DOI: https://doi.org/10.1155/2010/729457

IF: 3.791

2010-01-01

Journal of Nanomaterials

Abstract:A novel bone-like biomaterial of hydroxyapatite (HAP) and silk fibroin (SF) composite was developed by biomimetic synthesis. The composite was precipitated from drops of Ca ( OH ) 2 suspension and H 3 PO 4 solution with SF. With this method, the HAP nanocrystals were obtained by self-assembling on a SF surface whose c-axis was aligned with the long-axis direction of SF in microstructures; this shares the same misconstrues of collagen and HAP with that in the natural bone. The HAP/SF composite then demonstrated that it could promote osteoblast proliferation in vitro and new bone formation in vivo . The novel biomaterial is a promising material for bone replacement and regeneration.

materials science, multidisciplinary,nanoscience & nanotechnology
Hierarchical biomineralization of calcium carbonate regulated by silk microspheres

Xiuli Zhang,Zhihai Fan,Qiang Lu,Yongli Huang,David L. Kaplan,Hesun Zhu

DOI: https://doi.org/10.1016/j.actbio.2013.03.004

IF: 10.633

2013-06-01

Acta Biomaterialia

Abstract:As an analog of the main protein contained in nacre regenerated Bombyx mori silk fibroin has a significant influence on the morphology and polymorphic nature of CaCO3 in the biomineralization process. A number of studies have implied that the self-assembling aggregate structure of silk fibroin is a key factor in controlling CaCO3 aggregation. Further insight into this role is necessary with a particular need to prepare silk fibroin aggregates with homogeneous structures to serve as templates for the mineralization process. Here we have prepared homogeneous silk microspheres to serve as templates for CaCO3 mineralization in order to provide an experimental insight into silk-regulated crystallization processes. CaCO3 particles with different nano- and microstructures, and their polymorphs, were successfully formed by controlling the mineralization process. The key function of silk aggregation in controlling the morphology and polymorphic nature of CaCO3 particles was confirmed. A regulating effect of silk on the spatial features was also observed. A two-step process for silk fibroin-regulated biomineralization was found, with different levels of heterogeneous nucleation and aggregation. A full understanding of silk fibroin-regulated biomineralization mechanisms would help in understanding the function of organic polymers in natural biomineralization, and provide a way forward in the design and synthesis of new materials in which organic-inorganic interfaces are the keys to function, biological interfaces and many related material features.

engineering, biomedical,materials science, biomaterials
Novel synthesis of hydroxyapatite microtubes using gelatin as sacrificial templates and their potential as biocompatible cell supporting matrix

Yajia Bai,Fenghao Zhang,Song Chen,Jianan Zhang,Toshiyuki Ikoma,Xiaona Li,Weiyi Chen

DOI: https://doi.org/10.1016/j.matlet.2023.134370

IF: 3

2023-04-13

Materials Letters

Abstract:Hydroxyapatite microtubes (HAp MTs) were synthesized through in situ deposition of HAp nanoparticles on the gelatin microfibers as novel sacrificial templates via a bio-mineralization route followed by a sintering process. The synthesized HAp MTs were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier-transform infrared spectroscopy (FT-IR). SEM images reveal that HAp MTs had uniform tubular hollow structures with a diameter of 50–200 μm. XRD patterns indicate that HAp MTs were mainly constructed by apatite phase. Cytotoxic evaluation shows that HAp MTs were not cytotoxic and well biocompatible with osteoblast MC3T3-E1 cells. Most importantly, each individual HAp MT supported cell attachment and proliferation, indicating a potential as biocompatible cell supporting matrix.

materials science, multidisciplinary,physics, applied
Surface coating of hydroxyapatite on silk nanofiber through biomineralization using ten times concentrated simulated body fluid and the evaluation for bone regeneration

Min Jung Lee,Jong Bo Park,Hyung Hwan Kim,Chang Seok Ki,Sook Young Park,Hyun Jeong Kim,Young Hwan Park

DOI: https://doi.org/10.1007/s13233-014-2114-x

IF: 2.127

2014-07-01

Macromolecular Research

Abstract:The biomineralization of hydroxyapatite (HA) on silk nanofiber surface was explored to create organic/inorganic composite scaffold for bone tissue engineering. The porous silk nanofibers matrix was prepared by electrospinning using methanol coagulation bath as a collector and the deposition and coating of HA crystals were proceeded through biomineralization process by immersing the nanofibers in ten times concentrated simulated body fluid (10X SBF). It was found that uniform surface coating of silk nanofibers with HA crystals can be easily obtained by using 10X SBF within short immersion time (60–90 min in this study). The morphological structure of the Silk/HA composite nanofiber was characterized by field emission scanning electron microscopy (FE-SEM) images and structural evidence of HA deposition onto the silk nanofibers were also performed by energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), and Fourier transform infrared (FTIR) spectroscopy. Methylthiazol tetrazolium (MTT) assay confirmed that the cell adhesion and proliferation of osteoblast cells on this composite scaffold was excellent and micro computed tomography (micro-CT) image also showed that better ability of bone regeneration occurred for the Silk/HA composite nanofiber scaffold after 8 weeks implantation. As a result of biological evaluation, the HA coated silk nanofiber scaffold can have a high potential for using in bone tissue regeneration.

polymer science
Biomimetic Nucleation of Hydroxyapatite Crystals Mediated by Antheraea pernyi Silk Sericin Promotes Osteogenic Differentiation of Human Bone Marrow Derived Mesenchymal Stem Cells

Mingying Yang,Yajun Shuai,Can Zhang,Yuyin Chen,Liangjun Zhu,Chuanbin Mao,Hongwei OuYang

DOI: https://doi.org/10.1021/bm401740x

2014-03-26

Biomacromolecules

Abstract:Biomacromolecules have been used as templates to grow hydroxyapatite crystals (HAps) by biomineralization to fabricate mineralized materials for potential application in bone tissue engineering. Silk sericin is a protein with features desirable as a biomaterial, such as increased hydrophilicity and biodegradation. Mineralization of the silk sericin from Antheraea pernyi (A. pernyi) silkworm has rarely been reported. Here, for the first time, nucleation of HAps on A. pernyi silk sericin (AS) was attempted through a wet precipitation method and consequently the cell viability and osteogenic differentiation of BMSCs on mineralized AS were investigated. It was found that AS mediated the nucleation of HAps in the form of nanoneedles while self-assembling into β-sheet conformation, leading to the formation of a biomineralized protein based biomaterial. The cell viability assay of BMSCs showed that the mineralization of AS stimulated cell adhesion and proliferation, showing that the resultant AS biomaterial is biocompatible. The differentiation assay confirmed that the mineralized AS significantly promoted the osteogenic differentiation of BMSCs when compared to nonmineralized AS as well as other types of sericin (B. mori sericin), suggesting that the resultant mineralized AS biomaterial has potential in promoting bone formation. This result represented the first work proving the osteogenic differentiation of BMSCs directed by silk sericin. Therefore, the biomineralization of A. pernyi silk sericin coupled with seeding BMSCs on the resultant mineralized biomaterials is a useful strategy to develop the potential application of this unexplored silk sericin in the field of bone tissue engineering. This study lays the foundation for the use of A. pernyi silk sericin as a potential scaffold for tissue engineering.

polymer science,biochemistry & molecular biology,chemistry, organic
Biofunctionalization of electrospun fiber membranes by LbL-collagen/chondroitin sulfate nanocoating followed by mineralization for bone regeneration

Jing Zheng,Naureen Rahman,Longfei Li,Jingshuang Zhang,Haozhe Tan,Yun Xue,Yu Zhao,Jiliang Zhai,Nana Zhao,Fujian Xu,Liqun Zhang,Rui Shi,Yuri Lvov,Jiajia Xue

DOI: https://doi.org/10.1016/j.msec.2021.112295

2021-01-01

Abstract:It is of great significance to develop osteoinductive artificial scaffold for bone repair and regeneration. We constructed a biomimetic apatite interface on electmspun polycaprolactone fibers by combining layer-by-layer (LbL) nanocoating with mineralization to fabricate an osteoinductive artificial scaffold. After polydopamine modification, cationic type-1 collagen and anionic chondroitin sulfate were sequentially adsorbed on the fiber surface. The fibers coated with the multilayer components served as the precursor matrix to induce apatite deposition. By adjusting the number of the layers and duration of mineralization, the nanoscale morphology of composite fibers was optimized. When ten bilayers of the collagen and chondmitin sulfate were deposited onto the fibers followed by one day-mineralization, the obtained polycaprolactone-apatite composite scaffolds significantly promoted the adhesion, proliferation, and osteogenic differentiation of MC3T3-E1 cells. In a subcutaneous implantation in mice, this composite fiber membrane enhanced in vivo ectopic osteogenesis. Our nanoarchitectural scaffolds were able to mimic the composition and structure of the bone matrix to a certain extent, holding great potential for bone repair and regeneration.
Protein Biomineralized Nanoporous Inorganic Mesocrystals with Tunable Hierarchical Nanostructures.

Xiang Fei,Wei Li,Zhengzhong Shao,Stefan Seeger,Dongyuan Zhao,Xin Chen

DOI: https://doi.org/10.1021/ja509334x

IF: 15

2014-01-01

Journal of the American Chemical Society

Abstract:Mesocrystals with the symmetry defying morphologies and highly ordered superstructures composed of primary units are of particular interest, but the fabrication has proved extremely challenging. A novel strategy based on biomineralization approach for the synthesis of hematite mesocrystals is developed by using silk fibroin as a biotemplate. The resultant hematite mesocrystals are uniform, highly crystalline, and porous nanostructures with tunable size and morphologies by simply varying the concentration of the silk fibroin and iron(III) chloride in this biomineralization system. In particular, we demonstrate a complex mesoscale biomineralization process induced by the silk fibroin for the formation of hematite mesocrystals. This biomimetic strategy features precisely tunable, high efficiency, and low-cost and opens up an avenue to access new novel functional mesocrystals with hierarchical structures in various practical applications.
Study of synthesis of nano-hydroxyapatite using a silk fibroin template

Jing Wang,Feng Yu,Lijie Qu,Xiangcai Meng,G Wen

DOI: https://doi.org/10.1088/1748-6041/5/4/041002

IF: 4.103

2010-08-01

Biomedical Materials

Abstract:Nano-hydroxyapatite (HA) was directly synthesized on a silk fibroin (SF) template using the property of SF being soluble in a concentrated CaCl(2) solution as a HA source of calcium at pH 7.4 and room temperature. The microstructure and bonding state were investigated by x-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry-thermogravimetry analysis (DSC-TG) and transmission electron microscopy (TEM). The results indicated that the HA crystals were poorly crystallized with a rod-like shape of 20-60 nm length and 10-20 nm diameter. Strong molecular interactions and chemical bonds might be present between SF and HA. There were other nucleation sites such as carbonyl (-C-O) and amine (-N-H-) groups on SF molecules besides the carboxyl (-COOH) and hydroxyl (-OH) groups previously reported. During the formation of HA, the coordination action between specific functional groups on SF and calcium ions (Ca(2+)) played an important role. The crystallinity of HA was improved and had an orientation growth along (0 0 2) at the presence of SF, resulting in a structure similar to natural bone. It was concluded that SF could regulate the structure and morphology of HA effectively.

engineering, biomedical,materials science, biomaterials

Formation of Hierarchical Bone-Like Apatites on Silk Microfiber Templates Via Biomineralization

Characterization and Cytocompatibility of Premineralized Silk Fibroin/Chitosan Composite Scaffolds

Effects of Different Structure Silk Fibroin on Crystallization of Hydroxyapatite

Air-plasma Treatment Promotes Bone-Like Nano-Hydroxylapatite Formation on Protein Films for Enhanced in Vivo Osteogenesis

Mineralization and Biocompatibility of Antheraea Pernyi (A. Pernyi) Silk Sericin Film for Potential Bone Tissue Engineering

Antheraea pernyi silk sericin mediating biomimetic nucleation and growth of hydroxylapatite crystals promoting bone matrix formation.

Growth Of Hydroxyapatite Crystals On Bombyx Mori (B. Mori) Silk Fibroin

Biomineralization of Natural Collagenous Nanofibrous Membranes and Their Potential Use in Bone Tissue Engineering.

Nucleation of Hydroxyapatite on Antheraea Pernyi (A. Pernyi) Silk Fibroin Film

Silk as templates for hydroxyapatite biomineralization: A comparative study of Bombyx mori and Antheraea pernyi silkworm silks

Silk Protein-Mediated Biomineralization: From Bioinspired Strategies and Advanced Functions to Biomedical Applications

Biomimetic Synthesis and Biocompatibility Evaluation of Carbonated Apatites Template-Mediated by Heparin.

In Vitro Growth of Bioactive Nanostructured Apatites Via Agar-Gelatin Hybrid Hydrogel.

A Novel Nanocomposite Particle of Hydroxyapatite and Silk Fibroin: Biomimetic Synthesis and Its Biocompatibility

Hierarchical biomineralization of calcium carbonate regulated by silk microspheres

Novel synthesis of hydroxyapatite microtubes using gelatin as sacrificial templates and their potential as biocompatible cell supporting matrix

Surface coating of hydroxyapatite on silk nanofiber through biomineralization using ten times concentrated simulated body fluid and the evaluation for bone regeneration

Biomimetic Nucleation of Hydroxyapatite Crystals Mediated by Antheraea pernyi Silk Sericin Promotes Osteogenic Differentiation of Human Bone Marrow Derived Mesenchymal Stem Cells

Biofunctionalization of electrospun fiber membranes by LbL-collagen/chondroitin sulfate nanocoating followed by mineralization for bone regeneration

Protein Biomineralized Nanoporous Inorganic Mesocrystals with Tunable Hierarchical Nanostructures.

Study of synthesis of nano-hydroxyapatite using a silk fibroin template