Abstract:Lithium-ion batteries (LIBs) that can be charged faster while delivering high capacity are currently in significant demand, especially for electric vehicle applications. In this context, this study introduces a less-explored subject: nitrogen and oxygen dual-doped carbons derived from bio-based copolymers, specifically poly(benzimidazole- co -amide). The synthesis involved varying proportions of benzimidazole to amide, namely, 8.5 : 1.5, 7 : 3, and 5 : 5. The copolymers were pyrolyzed under a nitrogen atmosphere to obtain co-doped carbons, wherein the copolymers acted as single sources of carbon, nitrogen, and oxygen, with the nitrogen content ranging between 12.1 and 8.0 at% and oxygen doping between 11.8 and 25.0 at%, and were named as pyrolyzed polybenzimidazole- co -amide 8.5–1.5, 7–3, and 5–5. Coin cells were fabricated and rate studies were conducted for all three samples, wherein PYPBIPA8.5–1.5 outperformed all others, especially at higher current densities. Intrigued by these interesting results, when long-cycling studies were performed at a high current density of 4.0 A g −1 , pyrolysed polybenzimidazole- co -amide 8.5–1.5 showed a delithiation capacity of 135 mA h g −1 compared to pyrolysed polybenzimidazole- co -amide 7–3 and 5–5 with a delithiation capacity of 100 mA h g −1 and 60 mA h g −1 , respectively, with a capacity retention of 90% even after 3000 cycles. Furthermore, a full cell (2025-coin cell) was fabricated using the PYPBIPA8.5–1.5 anode and LiNi 0.80 Co 0.15 Al 0.05 O 2 (LiNCAO) cathode.

A Nitrogen-Containing Carbon Film Derived from Vapor Phase Polymerized Polypyrrole As a Fast Charging/discharging Capability Anode for Lithium-Ion Batteries.

Robust and Fast Lithium Storage Enabled by Polypyrrole-Coated Nitrogen and Phosphorus Co-Doped Hollow Carbon Nanospheres for Lithium-Ion Capacitors

In Situ Gas-Phase Polymerization of Polypyrrole-Coated Lithium-Rich Nanotubes for High-Performance Lithium-Ion Batteries

Energy efficient and fast charging nitrogen doped carbon anodes derived from BIAN‐melamine based porous organic polymer for lithium‐ion batteries

A Tripartite Composite Incorporating Nitrogen-Doped Graphene Oxide, Polypyrrole, and Silica for Lithium-Ion Battery Anodes

Bio-based poly(benzimidazole-co-amide)-derived N, O co-doped carbons as fast-charging anodes for lithium-ion batteries

Extremely fast charging lithium-ion battery using bio-based polymer-derived heavily nitrogen doped carbon.

Graphdiyne Containing Atomically Precise N Atoms for Efficient Anchoring of Lithium Ion

Polypyrrole‐carbon Fiber Composite Film Prepared by Chemical Oxidative Polymerization of Pyrrole

Polypyrrole coated δ-MnO 2 nanosheet arrays as a highly stable lithium-ion-storage anode.

3D N-doped mesoporous carbon/SnO2 with polypyrrole coating layer as high-performance anode material for Li-ion batteries

Synergy and Symbiosis Analysis of Capacity-Contributing Polypyrrole and Carbon-Coated Lithium Iron Phosphate Nanostructures for High-Performance Cathode Materials

Polypyrrole coated δ-MnO2 nanosheet arrays as a highly stable lithium-ion-storage anode

Coaxial Co3O4@polypyrrole Core-Shell Nanowire Arrays for High Performance Lithium Ion Batteries

Fabrication of Carbon Nanofiber-Driven Electrodes from Electrospun Polyacrylonitrile/Polypyrrole Bicomponents for High-Performance Rechargeable Lithium-Ion Batteries

Porous nitrogen-doped Sn/C film as free-standing anodes for lithium ion batteries

Polytriphenylamine: A high power and high capacity cathode material for rechargeable lithium batteries

Facile synthesis and high lithium storage properties of mesoporous polypyrrole coated CoFe2O4 nanofibers

Flexible SnO2 /N-Doped Carbon Nanofiber Films as Integrated Electrodes for Lithium-Ion Batteries with Superior Rate Capacity and Long Cycle Life.

Preparation and Electrochemical Characterisation of Polypyrrole-Coated Li 2 SnO 3 Anode Materials for Lithium-Ion Batteries

Enhanced Rate Capability of Multi-Layered Ordered Porous Nickel Phosphide Film As Anode for Lithium Ion Batteries