Polypyrrole/Manganese Oxide Hybrid Coaxial Arrays for High-Performance Li-O2 Battery
Qiuming Gao,Zeyu Li,Zhengping Liu
DOI: https://doi.org/10.1149/ma2014-03/2/77
2014-01-01
ECS Meeting Abstracts
Abstract:With the increasing demand for high-performance battery by electric vehicle and the energy storage of power, the lithium-oxygen (Li-O2) battery has attracted much attention recently because of the extremely high theoretical energy density of 3505 Wh kg (including O2). However, there are still a number of challenges to limit the practical applications of Li-O2 battery, such as power density, electrical energy efficiency, lifetime, cyclability, safety and cost. Conductive polymer is a usual conductive carbon electrode material. The polypyrrole is a promising candidate of support for Li-O2 battery owing to its high electric conductivity, high chemical and electrochemical stability, stable three-dimensional structure, ease of synthesis, good adhesion and especially the higher polarity than the carbon materials. In most Li-O2 batteries reported, catalyst and conductive carbon materials are mixed physically, which limited the uniformity of the electrode material. In this report, the catalyst and the conductive polymer were synthesized step-by-step to form a homogeneous system with catalytic property and electrical conductivity. The nanowire α-MnO2 [3] and γ-MnOOH [4] were synthesized as the catalyst by hydrothermal method. The polypyrrole was polymerized on the surface of the nanowires to form the coaxial arrays. The nanowire α-MnO2 and γ-MnOOH were acted as not only the catalyst of the system, but also the template for the formation of the polypyrrole nanotubes. The hybrid systems were coaxial arrays. The XRD patterns and SEM images of the α-MnO2, γ-MnOOH and the coaxial array hybrids were given in Figure 1. The polypyrrole /manganese oxide hybrid coaxial arrays exhibited good electrochemical characteristics as Li-O2 battery electrode materials. With the current density of 0.1 mA cm, the specific discharge capacity exhibited 11846 mAh g (polypyrrole/α-MnO2 hybrid) and 4252 mAh g -1 (polypyrrole/γ-MnOOH hybrid), respectively. 10 20 30 40 50 60 70 80 50