Abstract:First thermoelectric properties measurements on bulk nanostructured Ba8Ga16Ge30 clathrate-I are presented. A sol-gel-calcination route was developed for preparing amorphous nanosized precursor oxides. The further reduction of the oxides led to quantitative yield of crystalline nanosized Ba8Ga16Ge30 clathrate-I. TEM investigations show the clathrate nanoparticles retain the size and morphology of the precursor oxides. The clathrate nanoparticles contain mainly thin plates (approx. 300 nm x 300 nm x 50 nm) and a small amount of nanospheres (diameter ~ 10 nm). SAED patterns confirm the clathrate-I structure type for both morphologies. The powders were compacted via Spark Plasma Sintering (SPS) to obtain a bulk nano-structured material. The Seebeck coefficient S, measured on low-density samples (53% of {\delta}x-ray), reaches -145 {\mu}V/k at 375 °C. The ZT values are quite low (0.02) due to the high resistivity of the sample (two orders of magnitude larger than bulk materials) and the low sample density. The trend of the temperature dependence of S is in agreement with the values obtained from electronic structure calculations and semi-classical Boltzmann transport theory within the constant scattering approximation. The total thermal conductivity (1.61 W/mK), measured on high density samples (93% of {\delta}x-ray), shows a reduction of 20-25% in relation to the bulk materials (2.1 W/mK). A further shaping of the sample for the Seebeck coefficient and electrical conductivity measurements was not possible due to the presence of cracks. An improvement on the design of the pressing tools, loading of the sample and profile of the applied pressure will enhance the mechanical stability of the samples. These investigations are now in progress.

Revealing uncommon transport in the previously unascertained very low cation clathrate-I Eu2Ga11Sn35

Chemical physics of metallic clathrates with low carrier concentration

Large Positive and Negative Magnetoresistance in the Magnetic EuCu4As2 Crystal

Unusual Magnetic and Transport Properties in the Zintl Phase Eu_11Zn_6As_12

Intrinsic insulating transport characteristics in low-carrier density EuCd2As2 films

Unusual magnetic and transport properties in the Zintl phase Eu$_{11}$Zn$_6$As$_{12}$

Thermal Transport in Thermoelectric Materials with Chemical Bond Hierarchy

Direct Observation of Above-Quantum-step Quasibound States Ingaas/alx

Structure, Thermal, And Transport Properties Of The Clathrates Sr8zn8ge38, Sr8ga16ge30, And Ba8ga16si30

Absence of metallicity and bias-dependent resistivity in low-carrier-density EuCd2As2

Monoclinic EuSn$_2$As$_2$: A Novel High-Pressure Network Structure

Absence of Weyl nodes in EuCd$_2$As$_2$ revealed by the carrier density dependence of the anomalous Hall effect

Enhanced conduction band density of states in intermetallic EuTSi3 (T = Rh, Ir)

Monoclinic : A Novel High-Pressure Network Structure

Unconventional transverse transport above and below the magnetic transition temperature in Weyl semimetal EuCd$_2$As$_2$

Unique structure type and antiferromagnetic ordering in semiconducting Eu2InSnP3

Nanostructuring of Ba8Ga16Ge30 clathrates

Single-crystal growth, structure and thermal transport properties of the metallic antiferromagnet Zintl-phase β-EuIn2As2

Non-collinear 2k antiferromagnetism in the Zintl semiconductor Eu$_5$In$_2$Sb$_6$