Influence of tannic acid post-treatment on the degradation and drug release behavior of Schiff base crosslinked konjac glucomannan/chitosan hydrogel

Yuqian Wu,Weijie Xu,Jianliang Li,Zhangfeng Zhong,Liqing Huang,Shengke Li,Huaping Tan

DOI: https://doi.org/10.1016/j.eurpolymj.2023.112592

IF: 6

2024-01-01

European Polymer Journal

Abstract:Dynamic Schiff base-mediated natural polysaccharide hydrogels are often griped about rapid degradation as biological scaffolds, which is desirable for an efficient method to improve their stability. Herein, tannic acid (TA) was employed to further entangle Schiff base crosslinked hydrogel (CSGM) composed of carboxymethyl chitosan (CMCS) and oxidized konjac glucomannan (OKGM) to achieve tunable degradation and drug release of the obtained CSGM@TA hydrogel. As examined by SEM, the porous structure of CSGM hydrogel became denser after being immersed in TA solution, and the average pore size of CSGM hydrogel was decreased from 108.0 μm to 60.0 μm along with TA amount in CSGM@TA hydrogel. The degradation rate of CSGM hydrogel was remarkably inhibited upon entanglement by TA. CSGM@TA-3 with highest TA amount was found stable in PBS (pH 5.5) after 14 days, whereas ∼ 50 % of CSGM hydrogel was remained under same condition. The release of TA from CSGM@TA hydrogels was also examined under different pH, and the total TA release from three CSGM@TA hydrogels was 10 %–19 % within 14 days at pH 5.5, whereas the value was remarkably increased to 35 %–45 % at pH 7.4, suggesting a pH-dependent TA release behavior controlled by pH-responsive Shiff-base bonding and TA-CSGM bonding. Meanwhile, CSGM@TA hydrogels were found to possess good antioxidant, antibacterial, and anti-biofilm capabilities, demonstrating great potential as multifunctional scaffolds for tissue engineering and wound healing.

polymer science

What problem does this paper attempt to address?

This paper primarily explores the effects of tannic acid (TA) post-treatment on the degradation behavior and drug release characteristics of Schiff base cross-linked konjac glucomannan/chitosan hydrogels (CSGM).

### Research Background and Objectives

- **Research Background**: Natural polysaccharide hydrogels mediated by dynamic Schiff bases often face the issue of rapid degradation when used as biological scaffolds, which limits their clinical applications in certain situations.
- **Research Objectives**: To achieve controlled degradation and drug release behavior by further entangling Schiff base cross-linked hydrogels (composed of carboxymethyl chitosan (CMCS) and oxidized konjac glucomannan (OKGM)) with tannic acid.

### Main Findings

1. **Microstructure Changes**: Scanning electron microscopy (SEM) showed that after soaking CSGM hydrogels in tannic acid solution, their porous structure became denser, with the average pore size reduced from 108.0 μm to 60.0 μm.
2. **Improved Degradation Performance**: The addition of tannic acid significantly inhibited the degradation rate of CSGM hydrogels in phosphate-buffered saline (PBS). Notably, CSGM@TA-3 (containing the highest amount of tannic acid) remained stable in PBS at pH 5.5 for 14 days, while untreated CSGM hydrogels retained only about 50% under the same conditions.
3. **Drug Release Characteristics**: The release of tannic acid from CSGM@TA hydrogels was pH-regulated, with a total release of 10%-19% at pH 5.5 over 14 days, increasing to 35%-45% at pH 7.4.
4. **Multifunctionality**: CSGM@TA hydrogels exhibited good antioxidant, antibacterial, and anti-biofilm capabilities, showing great potential as multifunctional scaffolds for tissue engineering and wound healing.

In summary, this study successfully improved the stability of Schiff base cross-linked hydrogels through tannic acid post-treatment and regulated their degradation behavior and drug release characteristics, providing new insights for the development of novel biomedical materials.