in vitro and in vivo Morphology and Degradation of Chitosan Based Thermosensitive Hydrogel as Drug Release Matrix

Jiang ZHAO,Guo-qiang JIANG,Jia-li SUN,Kuo ZHANG,Fu-xin DING

DOI: https://doi.org/10.3969/j.issn.1003-9015.2010.03.016

2010-01-01

Abstract:Chitosan/glycerophosphate (CTS/GP) thermosensitive hydrogel has great potentials in injectable drug delivery and tissue engineering. The project of the present study is to explore the morphology and degradation of CTS/GP hydrogel in vitro (PBS) and in vivo (subcutaneousness of SD rat). The pathological investigation shows that the CTS/GP hydrogel is enwrapped by a fiber capsule which can gradually attenuate, and the fiber tissue has the trend of inosculation with the hydrogel, which indicates that the CTS/GP hydrogel does not induce acute or chronic toxicity and is biological inertia. The effects of osmotic pressure, pH value, inflammation and tissue repair in vivo on CTS/GP hydrogel cause the significant differences in the morphology and degradation of CTS/GP hydrogel in vivo and in vitro. The inflammation and osmotic pressure lead dehydration on hydrogel, and its water content at 4 weeks after injection reduces to 89% in vivo, while the hydrogel undergoes a swelling process and its water content increases to 97% in vitro. Water loss of the hydrogel results in the more compact network structure and its porosity is 17% less than that in vitro. Due to the association and cross linking with the tissue, the M w of the hydrogel experiences the trend of increasing at first, then slowly decreasing in vivo. The degradation rate of the CTS/GP hydrogel in vivo is slower than that in vitro. The experimental results are advisable for the design of injectable implant based on hydrogel.