Abstract:Heterostructured nanoparticles have attracted significant attention due to its unique morphology and promotion of a wide range of applications. Among the different kinds of heterostructured nanomaterials, Au-ZnO core-shell nanoparticles have been widely used in dye-sensitized solar cells, photocatalysis, gas sensing and biological detection due to its distinctive physical and chemical properties. Understanding the growth behaviors of nanomaterials is essential for controlling their size, morphology and chemical composition, which can improve the applicability. However, the growth mechanisms of Au-ZnO core-shell nanoparticles are mostly suggested by the post-reaction investigations, and the direct observation of synthesis process is lacking but crucial. In this work, we utilized liquid cell transmission electron microscopy (LC-TEM) to observe the formation of Au-ZnO core-shell nanoparticles in real-time. The synthesis process of Au-ZnO core-shell nanoparticles was successfully demonstrated via in-situ LC-TEM (Figure 1). The solutions of zinc nitrate hexahydrate ( Zn(NO3)2 · 6H2O), hexamethylenetetramine (HMTA), ascorbic acid (AA) and hexadecyl trimethylammonium bromide (CTAB) were introduced into the liquid cell at the flow rate of 1 µl/min via the microchannels after Au nanoparticles dispersed. The citrate-stabilized Au nanoparticles attracted Zn(OH)4 2‒ complexes with the aid of CTAB and AA, and then Zn(OH)4 2‒ complexes would dehydrate and transform into loose ZnO shells around the Au cores. The morphology of ZnO shells was spherical and smooth, without any granular or crystalline appearance (Figure 2), which was suggested to result from absorbing CTAB molecules. In order to increase the crystallinity of ZnO shells by removing CTAB molecules, the Au-ZnO core-shell nanoparticles were heat-treated at 500°C for 2 h. The crystallization of ZnO shells followed by heat treatment could methodically control the microstructure of heterostructed nanoparticles (Figure 3). The growth behaviors, elements distribution and the statistics about growth has been systematically analyzed. This in-situ experiment casts light on preparation of Au-ZnO core-shell nanoparticles with function of CTAB and AA, extending the study of reaction mechanism and the improvement of controllability of heterostructure synthesis for further device application. Figure 1

Growth Of Au On Pt Icosahedral Nanoparticles Revealed By Low-Dose In Situ Tem

Characterization of Heterostructural Palladium Deposition on Spherical Gold Nanoparticles by in Situ Liquid Cell Transmission Electron Microscopy

A Mechanistic Study on the Nucleation and Growth of Au on Pd Seeds with a Cubic or Octahedral Shape

Controlling The Growth Of Au On Icosahedral Seeds Of Pd By Manipulating The Reduction Kinetics

Growth Mechanism Of Core-Shell Ptni-Ni Nanoparticles Using In Situ Transmission Electron Microscopy

Unravelling the Shell Growth Pathways of Au-Ag Core-Shell Nanoparticles by in Situ Liquid Cell Transmission Electron Microscopy.

Growth and Sintering of Au−Pt Nanoparticles on Oxidized and Reduced CeO<sub><i>x</i></sub>(111) Thin Films by Scanning Tunneling Microscopy

In situ TEM observation of Au-Cu2O core-shell growth in liquids

Anomalous Growth Rate of Ag Nanocrystals Revealed by in situ STEM

Growth and Structure of Cu and Au on the Nonpolar ZnO(101̅0) Surface: STM, XPS, and DFT Studies

Kinetically controlled overgrowth of Ag or Au on Pd nanocrystal seeds: from hybrid dimers to nonconcentric and concentric bimetallic nanocrystals.

Growth and Structure of Cu and Au on the Nonpolar ZnO(10(1)over-bar0) Surface: STM, XPS, and DFT Studies

Symmetric and asymmetric overgrowth of a Ag shell onto gold nanorods assisted by Pt pre-deposition

Deconvolution of Octahedral Pt 3 Ni Nanoparticle Growth Pathway from in Situ Characterizations

Nanosurface-confined nucleation and patterned growth of Pt and TiO2

Synthesis of Ultrathin Face‐Centered‐Cubic Au@ Pt and Au@ Pd Core–Shell Nanoplates from Hexagonal‐Close‐Packed Au Square Sheets

In Situ Observation of Au Nanostructure Evolution in Liquid Cell TEM

In Situstudy of Nucleation and Growth Dynamics of Au Nanoparticles on MoS2nanoflakes

Epitaxial growth of heterogeneous metal nanocrystals: from gold nano-octahedra to palladium and silver nanocubes.

Nucleation, Growth, and Adsorbate-Induced Changes in Composition for Co–Au Bimetallic Clusters on TiO2

Observing the Growth Mechanism of Au-ZnO Core-Shell Nanoparticles by In-Situ Liquid Cell TEM