Observing the Growth Mechanism of Au-ZnO Core-Shell Nanoparticles by In-Situ Liquid Cell TEM

Shin-Bei Tsai,Chih-Yang Huang,Jui-Yuan Chen,Wen-Wei Wu

DOI: https://doi.org/10.1149/ma2020-01452572mtgabs

2020-01-01

Abstract:Heterostructured nanoparticles have attracted significant attention due to its unique morphology and promotion of a wide range of applications. Among the different kinds of heterostructured nanomaterials, Au-ZnO core-shell nanoparticles have been widely used in dye-sensitized solar cells, photocatalysis, gas sensing and biological detection due to its distinctive physical and chemical properties. Understanding the growth behaviors of nanomaterials is essential for controlling their size, morphology and chemical composition, which can improve the applicability. However, the growth mechanisms of Au-ZnO core-shell nanoparticles are mostly suggested by the post-reaction investigations, and the direct observation of synthesis process is lacking but crucial. In this work, we utilized liquid cell transmission electron microscopy (LC-TEM) to observe the formation of Au-ZnO core-shell nanoparticles in real-time. The synthesis process of Au-ZnO core-shell nanoparticles was successfully demonstrated via in-situ LC-TEM (Figure 1). The solutions of zinc nitrate hexahydrate ( Zn(NO3)2 · 6H2O), hexamethylenetetramine (HMTA), ascorbic acid (AA) and hexadecyl trimethylammonium bromide (CTAB) were introduced into the liquid cell at the flow rate of 1 µl/min via the microchannels after Au nanoparticles dispersed. The citrate-stabilized Au nanoparticles attracted Zn(OH)4 2‒ complexes with the aid of CTAB and AA, and then Zn(OH)4 2‒ complexes would dehydrate and transform into loose ZnO shells around the Au cores. The morphology of ZnO shells was spherical and smooth, without any granular or crystalline appearance (Figure 2), which was suggested to result from absorbing CTAB molecules. In order to increase the crystallinity of ZnO shells by removing CTAB molecules, the Au-ZnO core-shell nanoparticles were heat-treated at 500°C for 2 h. The crystallization of ZnO shells followed by heat treatment could methodically control the microstructure of heterostructed nanoparticles (Figure 3). The growth behaviors, elements distribution and the statistics about growth has been systematically analyzed. This in-situ experiment casts light on preparation of Au-ZnO core-shell nanoparticles with function of CTAB and AA, extending the study of reaction mechanism and the improvement of controllability of heterostructure synthesis for further device application. Figure 1