Zintl Phase Yb 1– x Ba x Mg 2 Bi 1.98 Compounds with Enhanced Thermoelectric Performance Caused by Cation Substitution
Jing Wang,Fengkai Guo,Muchun Guo,Jianbo Zhu,Qian Zhang,Wei Cai,Jiehe Sui
DOI: https://doi.org/10.1021/acsaem.0c02019
IF: 6.4
2020-10-29
ACS Applied Energy Materials
Abstract:Contributing to the unique structural and chemical characteristics, AM<sub>2</sub>X<sub>2</sub> Zintl compounds with the CaAl<sub>2</sub>Si<sub>2</sub>-type structure present advanced thermoelectric properties. In the present work, for YbMg<sub>2</sub>Bi<sub>2</sub> compounds, the impact of Ba substitution on the Yb site is investigated. Owing to the changed electronegativity, the addition of Ba gives rise to the decline of carrier concentration and then induces the depressed power factor. However, fortunately, phonon scattering is dramatically intensified at the same time, which could be attributed to the obvious mass and strain fluctuation that originated from a visibly different mass/size between the Yb and Ba atoms. Typically, the lattice thermal conductivity of Yb<sub>0.75</sub>Ba<sub>0.25</sub>Mg<sub>2</sub>Bi<sub>1.98</sub> achieves 1.21 W m<sup>–1</sup> K<sup>–1</sup> with a decrease of 46% compared to that of pristine YbMg<sub>2</sub>Bi<sub>1.98</sub> at room temperature. Ultimately, for nontoxic Yb<sub>0.75</sub>Ba<sub>0.25</sub>Mg<sub>2</sub>Bi<sub>1.98</sub>, a significantly improved ZT value of ∼1.04 at 823 K is achieved. More importantly, the ZT<sub>eng</sub> value noticeably increases to ∼0.64 when <i>T</i><sub>h</sub> = 873 K and <i>T</i><sub>c</sub> = 300 K, with an enhancement of ∼46% compared with the initial one. Meanwhile, the characteristic of nontoxicity would also enhance the possibility of YbMg<sub>2</sub>Bi<sub>2</sub> to realize practical application.This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels