Abstract:Polysiloxane with multiple acryloxyl groups at the terminal site of the polymer chain was synthesized by the condensation reaction between hydroxyl-terminated polysiloxane and acryloyl chloride and used to improve the cross-linking density of UV-curable silicone materials initiated from dual acryloxy-terminated symmetric polysiloxane or single acryloxy-terminated asymmetric polysiloxane with the mixture of Irgacure 1173 and Irgacure 184 at a mass ratio of 1:1 as the photoinitiator. The effects of factors such as initiator composition, UV irradiation time, structure, and molecular weight of linear dual acryloxy-terminated or single acryloxy-terminated asymmetric siloxane oligomers on the gelation yield, thermal properties, water absorption, and water contact angle of UV-cured film were investigated. The synthesized cross-linking density modifier can be copolymerized with acryloxy-functionalized linear polysiloxanes under the action of a photoinitiator to increase the cross-link density of UV-cured products effectively. Both linear dual acryloxy-terminated or single acryloxy-terminated asymmetric siloxane oligomers can be copolymerized with cross-link density modifiers within 20 s of UV irradiation. The gelation yields of the UV-cured products obtained from the dual acryloxy-terminated siloxane oligomers were greater than 85%, and their surface water contact angles increased from 72.8° to 95.9° as the molecular weight of the oligomers increased. The gelation yields of UV-cured products obtained from single acryloxy-terminated asymmetric siloxane oligomers were less than 80%, and their thermal stabilities were inferior to those obtained from the dual acryloxy-terminated siloxane oligomers. However, the water contact angles of UV-cured products obtained from these single acryloxy-terminated asymmetric siloxane oligomers were all greater than 90°.

Novel hyperbranched polysiloxanes containing acetoacetyl groups synthesized through transesterification reaction.

Synthesis and Photopolymerization Kinetics of a Novel Monomer: 1,4-Butanediol Bis(alpha-Trimethylsiloxyacrylate): Steric Effect of the alpha-Trimethylsiloxy Substituent on the Reaction Kinetics

Polysiloxanes Polymers with Hyperbranched Structure and Multivinyl Functionality

A Novel Post-Polymerization Modification Route to Functional Poly(Disubstituted Acetylenes) Through Phenol-yne Click Reaction

Properties and Characterization of Novel Cationic Polyacrylate Latex Containing Fluorine and Silicon Prepared with Soap-Free Emulsion Polymerization

Synthesis and Characterization of Novel Non-conjugated hyperbranched polysiloxane with AIE Effect

A New Strategy of Post-Polymerization Modification to Prepare Functionalized Poly(disubstituted Acetylenes)

Polysilaethers bearing Si–H and its functionalization via hydrosilylation with acrylic acid

Hyperbranched Poly(ether-siloxane)s Containing Ammonium Groups: Synthesis, Characterization and Catalytic Activity

Synthesis and Characterization of Grafted Silicone Polycarbonates

Synthesis and Characterization of Hyperbranched and Organosilicone Modified Waterborne Polyurethane Acrylates Photosensitive Resin

Preparation and Thermal Stability of Phosphorus Acrylic Latex Modified with Organic Silicon

Silanization as a strategy to design polyurethane-acrylic hybrid pressure-sensitive adhesives

The Preparation of Acryloxyl Group Functionalized Siloxane Polymers and the Study of Their Ultra Violet Curing Properties

Synthesis and Performance of Novel Fluorinated Acrylate Polymers: Preparation and Reactivity of Short Perfluoroalkyl Group Containing Monomers

Synthesis and application of adhesion promoter containing phenolic hydroxyl/acrylate groups for addition-cure liquid silicone rubber

Improving Thermal Stability of Polyurethane through the Addition of Hyperbranched Polysiloxane

The Preparation and Surface Properties of Silicone-grafted Acrylic Copolymer Coatings

Preparation of organosilicon and organofluorine synergistically modified amphiphilic branched polyurethanes and their application in diisocyanate emulsifiers

Synthesis and Characterization of Novel Functional Hyperbranched Polyesters