Abstract:Previously, it was a challenge to develop a direct and convenient synthetic means for production of anisotropic particles, formation of structures (core-shell, cavity, hollow, etc.) and functionalization of domains all at once. Herein, we present a simple one-step dispersion polymerization (Dis.P) approach to synthesize particles with a combination of anisotropies in morphology, surface roughness, structure and composition. This approach needs no delayed addition of agents, and is of comparable simplicity to the preparation of conventional spherical particles. A cross-linker of dimethacryloyloxybenzophenone (DMABP) is added at the beginning of Dis.P of styrene (St). Evolution of monomer conversion, particle gel content and morphology during Dis.P indicates that DMABP is consumed early and rapidly, creating a high cross-linking of a growing particle at a low conversion, thus inducing phase separation and producing snowman-or dumbbell-like particles which contain a firstly cross-linked, coarse growing particle domain (G domain) and an uncross-linked or subsequently cross-linked, smooth, new domain (N domain). The size, surface roughness, structure and composition of the domains are tuned by initially adding various amounts of DMABP and a low amount of functional monomers. Due to the quick reaction of hydrophilic 4-vinylpyridine (4-VP), glycidyl methacrylate (GMA) or methacrylic acid (MAA), the G domain is enriched with pyridyl, epoxy or carboxyl groups, as detected by XPS and EDS. Through the delayed reaction of monomers containing alkynyl groups (-C equivalent to C-), the N domain is enriched with -C equivalent to C-groups, and the core-shell (cross-linked) structure is formed. With aids of thiols added during Dis.P, SH- or fluorine-containing groups are primarily incorporated on the N domain, and the porous, cavity or hollow structure of the N domain is generated due to phase separation between polystyrene (PSt) and the polymer produced by the click reaction. On adding two functional monomers (MAA and monomer containing -C equivalent to C-groups), various functional groups enrich G and N domains, respectively, owing to the sequential reactions of monomers.

Facile Synthesis of Core-Shell, Multiple Compartment Anisotropic Particles Via Control of Cross-Linking and Continuous Phase Separations in One-Pot Dispersion Polymerization

Direct One-Pot Synthesis of Chemically Anisotropic Particles with Tunable Morphology, Dimensions, and Surface Roughness

Control of cross-linking and reactions in one-step dispersion polymerization toward particles with combined anisotropies

Morphology Control of Anisotropic Nonspherical Functional Polymeric Particles by One-Pot Dispersion Polymerization

Controllable Synthesis of Anisotropic Silica/polymer Composite Particles Via Seeded Dispersion Polymerization

Facile Synthesis of Single‐Hole Crosslinked Particles with Embedded Single Bulge by Seeded Emulsion Polymerization

Fabrication of Poly(styrene-co-acrylic Acid)/polystyrene Anisotropic Nanoparticles Via Seeded Emulsion Polymerization

Formation Of Monodisperse Polymer@Sio2 Core-Shell Nanoparticles Via Polymerization In Emulsions Stabilized By Amphiphilic Silica Precursor Polymers: Hlb Dictates The Reaction Mechanism And Particle Size

Anomalously Shaped Functional Particles Prepared by Thiol-Isocyanate Off-Stoichiometric Click Dispersion Polymerization

Synthesis of Latex Particles with a Complex Structure As an Emulsifier of Pickering High Internal Phase Emulsions

Facile Fabrication of Anisotropic Colloidal Particles with Controlled Shapes and Shape Dependence of Their Elastic Properties

Shape-Anisotropic Diblock Copolymer Particles with Varied Internal Structures

Shape-Tunable Biconcave Disc-Like Polymer Particles by Swelling-Induced Phase Separation of Seeded Particles with Hydrophilic Shells

Facile Synthesis of Large Scale and Narrow Particle Size Distribution Polymer Particles Via Control Particle Coagulation During One-Step Emulsion Polymerization

Synthesis of Anisotropic Polymer/Inorganic Particles Via Asymmetric Swelling-Dissolving Process

The Morphological Control of Anisotropic Polystyrene/silica Hybrid Particles Prepared by Radiation Miniemulsion Polymerization

Anisotropic Nanoparticles with Controllable Morphologies from Non-Cross-Linked Seeded Emulsion Polymerization

New route to monodispersed amphiphilic core-shell polymer nanoparticles: Polymerization of styrene from α-methylstyrene-containing macroinitiator

Synthesis of Large-Scale, Narrowly Dispersed, Highly Cross-Linked, and Spherical Latex Particles Via One-Step Emulsion Polymerization Through Particle Coagulation

Anisotropic particles from a one-pot double emulsion induced by partial wetting and their triggered release.

Janus Anisotropic Hybrid Particles with Tunable Size from Patchy Composite Spheres