An Ionic Liquid-Present Method for Preparing Micro-sized Octahedral Particles of Co3O4 and Their Applications As Anode Materials for Lithium Ion Batteries
Keqiang Ding,Xiaojing Gao,Jingwei Han,Xiangming He,Runling Qu,Lanjun Zhou,Hongmin Dou,Hui Wang,Li Wang
DOI: https://doi.org/10.20964/2020.05.83
IF: 1.541
2020-01-01
International Journal of Electrochemical Science
Abstract:For the first time, tricobalt tetraoxide (Co3O4) particles with a well-defined octahedral structure and a size more than 8 mu m were prepared via an ionic liquid-present dissolving-drying-calcination method using cobaltous acetate tetrahydrate (Co(CH3COO)(2)center dot 4H(2)O) as the precursor in this work. Different from the previous works, a kind of ionic liquids (ILs) was employed as one main component of the preparation solution. The materials prepared in the presence of 1-butyl-3-methylimidazolium bromide, 1-butyl-3-methylimidazolium tetrafluoroborate and 1-butyl-3-methylimidazolium chloride were respectively nominated as material a, b and c. As indicated by the XRD and XPS analysis, CoO and Co3O4 were the major components of material a and b, and Co3O4 was the main substance of material c. As confirmed by the obtained SEM images, octahedral particles of Co3O4 with a size greater than 8 mu m were prepared in material c. When being used as anode materials for lithium ion batteries (LIBs), material a, b and c at the current density of 100 mA g(-1) exhibited an initial discharge capacity of 600, 612 and 878 mAh respectively. Particularly, material c was able to deliver a discharge capacity of 336 mAh g(-1) after 10 cycles even under the current density of 500 mA g(-1). A fact that octahedral particles of Co3O4 with a size more than 8 mu m could be prepared using an ionic liquid-present method was presented in this work, which was very beneficial to the development of metal oxides based anode materials of LIBs as well as the exploration of micro-devices.