Abstract:Uniform, large-scale, and well-aligned needle-like ZnO nanorods with good photoluminescence and photocatalysis properties on Zn substrates, have been successfully fabricated using a simple low-temperature seed-layer growth approach in solution (50 °C). The formation of ZnO seed-layer by the anodic oxidation technique (AOT) plays an important role in the subsequent growth of highly oriented ZnO nanorods arrays. Temperature also proved to be a significant factor in the growth of ZnO nanorods and had a great effect on their optical properties. X-ray diffraction (XRD) analysis, selected-area electron diffraction (SAED) pattern and high-resolution TEM (HRTEM) indicated that the needle-like ZnO nanorods were single crystal in nature and that they had grown up preferentially along the [0001] direction. The well-aligned ZnO nanorods arrays on Zn substrates exhibited strong UV emission at around 380 nm at room temperature. To investigate their potential as photocatalysts, degradation of pentachlorophenol (PCP) in aqueous solution was carried out using photocatalytic processes, with comparison to direct photolysis. After 1 h, the degradation efficiencies of PCP by direct photolysis and photocatalytic processes achieved 57% and 76% under given experimental conditions, respectively. This improved degradation efficiency of PCP illustrates that ZnO nanorods arrays on Zn substrates have good photocatalytic activity. This simple low-temperature seed-layer growth approach in solution resulted in the development of an effective and low-cost fabrication process for high-quality ZnO nanorods arrays with good optical and photocatalytic properties that can be applicable in many fields such as photocatalysis, photovoltaic cells, luminescent sensors, and photoconductive sensors.

Low-temperature Solution Growth of ZnO Nanocone/highly Oriented Nanorod Arrays on Copper.

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Direct Solution Phase Fabrication of Zno Nanostructure Arrays on Copper at Near Room Temperature

Controllable Growth of Highly Oriented ZnO Nanorod Arrays on Copper by a Two-Step Route

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Solution Growth of ZnO Nanostructure Arrays on FTO Substrates at Near Room Temperature

Low temperature growth and properties of ZnO nanorod arrays

A Low-Temperature Aqueous Solution Route to Large-Scale Growth of Zno Nanowire Arrays

Fabrication of needle-like ZnO nanorods arrays by a low-temperature seed-layer growth approach in solution

Low-Temperature Synthesis and Optical Property of ZnO Nanorod Arrays

Controlled Growth and Photoluminescence of Highly Oriented Arrays of ZnO Nanocones with Different Diameters

Patterned growth of vertically aligned ZnO nanowire arrays on inorganic substrates at low temperature without catalyst

Patterned growth of vertically aligned ZnO nanowire arrays on inorganic substrates at low temperature without catalyst.

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Controllable Synthesis and Optical Properties of Novel ZnO Cone Arrays Via Vapor Transport at Low Temperature

A Simple Route to Controllable Growth of ZnOnanorod Arrays on Conducting Substrates

Highly Oriented 1-D Zno Nanorod Arrays on Zinc Foil: Direct Growth from Substrate, Optical Properties and Photocatalytic Activities

Vertically Aligned 1D ZnO Nanostructures on Bulk Alloy Substrates: Direct Solution Synthesis, Photoluminescence, and Field Emission

Low temperature thermal oxidation synthesis of ZnO nanoneedles and the growth mechanism

Solution growth of nano- to microscopic ZnO on Zn

One dimensional ZnO nanostrucures grown on ZnO/Si by hydrothermal process