Abstract:In this paper, porous zinc oxide (ZnO) nanosheets were successfully prepared by a simple low-temperature hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) tests showed that the synthesized product was ZnO with porous sheet structure. The diameter of porous nanosheets was about 100 nm and the thickness was about 8 nm. As a photocatalyst, the degradation efficiencies of porous ZnO nanosheets for methyl orange (MO), methylene blue (MB) and Rhodamine B (RhB) were 97.5%, 99% and 96.8%, respectively. In addition, the degradation efficiency of ZnO for mixed dyes (Mo, MB and RhB) was satisfactory, reaching 97.7%. The photocatalytic stability of MB was further tested and remained at 99% after 20 cycles. In the experiment, ZnO/FTO (fluorine-doped tin oxide) composites were prepared by using ZnO as the conductive layer. Titanium dioxide (TiO2) was deposited on the surface of ZnO/FTO by electrodeposition, so as to obtain a TiO2/ZnO/FTO composite. By studying the electrochromic properties of this composite, it was found that the TiO2/ZnO/FTO composite shows a large light modulation range (55% at 1000 nm) and excellent cycle stability (96.6% at 200 cycles). The main reason for the excellent electrochromic properties may be the synergistic effect between the porous structure and the polymetallic oxides. This study is helpful to improve the photocatalytic efficiency and cycling stability of metal oxides, improve the transmittance of thin films and provide a new strategy for the preparation of ZnO composite materials with excellent photocatalytic and electrochromic properties.

Facile synthesis of porous single crystalline ZnO nanoplates and their application in photocatalytic reduction of Cr(VI) in the presence of phenol

Facile Fabrication of Porous ZnO by a Template Free Method

High-ratio {100} Plane-Exposed ZnO Nanosheets with Dual-Active Centers for Simultaneous Photocatalytic Cr(VI) Reduction and Cr(III) Adsorption from Water

Enhanced Photocurrent and Photocatalytic Properties of Porous ZnO Thin Film by Ag Nanoparticles

Cr(VI) Reduction in Presence of ZnS/RGO Photocatalyst under Full Solar Spectrum Radiation from UV/vis to Near-Infrared Light

Synergistic photoelectrochemical reduction of Cr(VI) and oxidation of organic pollutants by g-C3N4/TiO2-NTs electrodes.

Porous Tube-Like ZnS Derived from Rod-Like ZIF-L for Photocatalytic Cr(VI) Reduction and Organic Pollutants Degradation

Metal–Organic Framework MIL-101(Fe) Nanoparticles Decorated with Ag Nanoparticles for Regulating the Photocatalytic Phenol Oxidation Pathway for Cr(VI) Reduction

Synthesis of the Porous ZnO Nanosheets and TiO2/ZnO/FTO Composite Films by a Low-Temperature Hydrothermal Method and Their Applications in Photocatalysis and Electrochromism

Facile construction of g-C3N4/ZnIn2S4 nanocomposites for enhance Cr(VI) photocatalytic reduction

Facile Synthesis of UCNPs/Zn X Cd 1-X S Nanocomposites Excited by Near-Infrared Light for Photochemical Reduction and Removal of Cr(VI)

Anatase Tio2 Nanoparticles Immobilized on Zno Tetrapods As A Highly Efficient and Easily Recyclable Photocatalyst

Photocatalytic reduction of Cr(VI) and Ni(II) in aqueous solution by synthesized nanoparticle ZnO under ultraviolet light irradiation: a kinetic study

Synthesis ofporous single-crystalline ZnO nanoplates and their sensing properties to indoor air pollutants

A facile solution synthesis of ZnO nanoplates on Al substrate at room temperature

Chemically controlled growth of porous CeO 2 nanotubes for Cr(VI) photoreduction

Controllable preparation and efficient visible-light-driven photocatalytic removal of Cr(VI) using optimized Cd0.5Zn0.5S nanoparticles decorated H-Titanate nanotubes

ZnO hierarchical structures with tunable oxygen vacancies for high performance in photocatalytic degradation of phenol

ZnS/ZnO nanosheets obtained by thermal treatment of ZnS/ethylenediamine as a Z-scheme photocatalyst for H<sub>2</sub> generation and Cr (VI) reduction

Tuning the Interfaces of ZnO/ZnCr2 O4 Derived from Layered-Double-Hydroxide Precursors to Advance Nitrogen Photofixation.

Porphyrin-based metal–organic frameworks loaded with Ag nanoparticles and their nanofibrous filters for the photocatalytic reduction of Cr(VI)