Conjoint analysis of online experiment and phase field simulation for the effect of metal hetero interface on diffusion of microwave sintering
Dan KANG,Feng XU,Xiao-fang HU,Yu XIAO
DOI: https://doi.org/10.7520/1001-4888-16-093
2018-01-01
Abstract:Alloy material has excellent mechanical properties and wide application,compared with traditional method,it has obvious advantage to prepare alloy by microwave.In order to explore the mechanism of microwave sintering alloymaterials,the Ti and Al mixed metal sample,which has high degree of concern in alloy domain,was adopted in this paper,microstructure evolution during microwave sintering was obtained by online experiment.By comparing with pure Ti and pure Al,it is found that the sintering temperature of mixed Ti-Al sample decreases significantly,and the sintering rate increases significantly.Analysis considers,intermetallic compound is formed between Ti and Al,which leads to interfacial polarization due to different conductivity.The polarization loss leads to the increase of temperature at interface and the diffusion rate of interface substance.Meanwhile,due to the intension of material diffusion at interface,a large number of atoms aggregates to sintering neck,resulting in the diffusion of vacancies to the grain boundary.Supersaturated vacancies are annihilated by the dislocations at grain boundaries,producing an local force that pulls neighboring particles toward one to another.Using the results of theoretical analysis,a variety of diffusion mechanism and rigid body motion were introduced,and the control equation of density field was modified,and the evolution curves of microstructure parameters such as sintering neck and so on were fitted.The curves and experimental results are basically consistent,which further verified that the mixture of metals and microwave produces a special effect,that is,the thermal effect driving material diffusion and the force acting on particle moving.Above results provide support for study of alloy evolution mechanism during microwave sintering process.