Conformational Transition and Interchain Association of Hypergraft HB-PS- g -P t BA Copolymer Chains with Varied Copolymer Compositions and Block Lengths in a Selective Solvent
Siqi Huang,Jinxian Yang,Nairong Hao,Muhammad Waqas Ishaq,Jun Wang,Naisheng Jiang,Lianwei Li
DOI: https://doi.org/10.1021/acs.macromol.1c01971
IF: 5.5
2022-04-15
Macromolecules
Abstract:Understanding the correlation between the solution phase behavior and topological effect of branched polymers is a fundamental problem in polymer physics. In this work, four sets of narrowly distributed hypergraft HB-PS-g-PtBA copolymers were prepared and studied, where PS and PtBA represent a polystyrene hyperbranched core and a poly(tert-butyl polyacrylate) periphery, respectively. The dispersity, branching pattern, block length, and copolymer composition were precisely controlled. In particular, the mass fraction (wt) of PtBA in HB-PS-g-PtBA was varied from 64 to 6.5% in a wide range. By combining laser light scattering (LLS), small-angle neutral scattering (SANS), and theoretical analysis, the temperature-dependent intrachain collapse and interchain association of HB-PS-g-PtBA chains were investigated in the temperature range lower than the θ point of the PS block in cyclohexane. By measuring the apparent aggregation number (N agg,app), the radius of gyration (⟨R g,app⟩), hydrodynamic radius (⟨R h,app⟩), form factor, aggregation pattern, existing species, segment density, internal structural features, and the degree of overlap (DO) of PtBA grafts were quantitatively analyzed. The result not only demonstrated that the hyperbranched topology can significantly suppress the aggregation tendency of the solvophobic hyperbranched PS core, irrespective of the copolymer composition, even though the wt of the PtBA solvophilic shell was decreased to as low as 15%, but also indicated that the DO value is the most important index that can reflect the ability of the graft layer in stabilizing the collapsed core structure.
polymer science