Ultraviolet and visible upconversion luminescence of Tm(0.1)Yb(5):FOV oxyfluoride nanophase vitroceramics
XiaoBo Chen,ZengFu Song,JinGuang Wu,N. Sawanoboi,M. Ohtsuka,YongLiang Li,Jing Zhou,Ce Wang,JinYing Liu,Qiang Tian,Ping Sun,HongMei Jing
DOI: https://doi.org/10.1007/s11433-008-0183-6
2008-01-01
Abstract:The ultraviolet upconversion luminescence of Tm 3+ ions sensitized by Yb 3+ ions in oxyfluoride nanophase vitroceramics when excited by a 975 nm diode laser was studied. An ultraviolet upconversion luminescence line positioned at 363.6 nm was found. It was attributed to the fluorescence transition of 1 D 2 → 3 H 6 of Tm 3+ ion. Several visible upconversion luminescence lines at 450.7 nm, (477.0 nm, 462.5 nm), 648.5 nm, (680.5 nm, 699.5 nm) and (777.2 nm, 800.7 nm) were also found, which result respectively from the fluorescence transitions of 1 D 2 → 3 F 4 , 1 G 4 → 3 H 6 , 1 G 4 → 3 F 4 , 3 F 3 → 3 H 6 and 3 H 4 → 3 H 6 of Tm 3+ ion. The careful measurement and analysis of the variation of upconversion luminescence intensity F as a function of the 975 nm pumping laser power P prove that the upconversion luminescence of 1 D 2 state is partly a five-photon upconversion luminescence, and the upconversion luminescence of 1 G 4 state and 3 H 4 state are respectively the three-photon and two-photon upconversion luminescence. The theoretical analysis suggested that the upconversion mechanism of the 363.6 nm 1 D 2 → 3 H 6 upconversion luminescence is partly the cross energy transfer of { 3 H 4 (Tm 3+ ), 3 F 4 (Tm 3+ ), 1 G 4 (Tm 3+ )→ 1 D 2 (Tm 3+ )} and { 1 G 4 (Tm 3+ )→ 3 F 4 (Tm 3+ ), 3 H 4 (Tm 3+ )→ 1 D 2 (Tm 3+ )} between Tm 3+ ions. In addition, the upconversion luminescence of 1 G 4 and 3 H 4 state results respectively from the sequential energy transfer { 2 F 5/2 (Yb 3+ )→ 2 F 7/2 (Yb 3+ ), 3 H 4 (Tm 3+ )→ 1 G 4 (Tm 3+ )} and { 2 F 5/2 (Yb 3+ ) → 2 F 7/2 (Yb 3+ ), 3 F 4 (Tm 3+ )→ 3 F 2 (Tm 3+ )} from Yb 3+ ions to Tm 3+ ions.