Frequency upconversion luminescence in Tm3+/Yb3+- and Ho3+/Yb3+-codoped Ga2O3–GeO2–Bi2O3–PbO glasses
D.M. Shi,Q.Y. Zhang,G.F. Yang,C. Zhao,Z.M. Yang,Z.H. Jiang
DOI: https://doi.org/10.1016/j.jallcom.2007.11.072
IF: 6.2
2008-01-01
Journal of Alloys and Compounds
Abstract:This paper reports on frequency upconversion emission properties of Tm3+/Yb3+- and Ho3+/Yb3+-codoped Ga2O3–GeO2–Bi2O3–PbO glass upon excitation of 980nm laser diode. The dependence of the upconversion emission intensity upon the excitation power has been examined and the involved mechanisms have also been discussed. An intense blue emission at 476nm and two weak red emissions at 650 and 689nm have clearly been observed in Tm3+/Yb3+-codoped samples, which are assigned to the 1G4→3H6, 1G4→3F4 and 3F2,3→3H6 transitions of Tm3+ ions. The cube-like dependence of the 476 and 650nm emissions on the incident pump laser power, indicates three-photon contribute to the blue–red upconversion emissions, respectively. Meanwhile intense green and red emissions peaked at 545 and 660nm in Ho3+/Yb3+-codoped samples, which are ascribed to the transitions of (5F4, 5S2)→5I8 and 5F5→5I8 transitions of Ho3+, have been confirmed that two photons contribute to these upconversion processes. The observed upconversion emission intensity as function of Yb3+ concentration suggests that the presence of the Yb2O3 plays a major role in enhancing the upconversion emission efficiency.