Abstract:Y2O3 : Tb3+ and Y2O3 : Tb3+, Yb3+ samples were prepared by co-precipitation method. The morphology, microstructure and fluorescence spectra at room temperature of samples were characterized by scanning electron microscopy(SEM) transmission electron microscopy(TEM), X-ray diffraction (XRD) and fluorescence spectrometer, The optimal process conditions of Y2O3 : Tb3+ under different doping concentrations, annealing temperature, and pH value of the solution were obtained: Tb3+ concentration is 1. 5% annealing temperature is 1 400 degrees C, an alkaline solution environment, and samples under 300 nm light excitation have the largest green light emission at 543 nm. The corresponding relation of Tb3+ ion level structure and transition properties and experimental spectra were analyzed in detail, and we explained the influence mechanism of process conditions and the fluorescence quenching process mainly effects luminous intensity of samples. The energy transfer from sensitizing ions Tb3+ to active ion Yb3+ was confirmed, it made the sample have considerable emitting light in the near-infrared region; the authors described the process of cooperation conversion luminescence between the two ions from the level transition angle, and also analyzed the system of fluorescence quenching process. Test results showed that the near infrared quantum cutting can effectively improve the luminous efficiency of doped ions, and will have broad application prospects in the silicon solar cells and other fields.

Multiphoton Near-Infrared Quantum Cutting Luminescence of Yb^3+ Ion Cooperative Energy Transferred from the Oxyfluoride Vitroceramics Phosphor Matrix

Near-Infrared Quantum Cutting Downconversion Luminescence of Yb3+Ion Cooperative Energy Transferred from YVO4 Matrix Donor

Preparation of Tb3+, Yb3+ doped Y2O3 luminescent powders and near-infrared quantum cutting research]

[Cooperative Downconversion in Tb (0.7 ) Yb (5) : FOV Oxyfluoride Nanophase Vitroceramics].

Visible-to-infrared quantum cutting by phonon-assisted energy transfer in YPO(4):Tm(3+), Yb(3+) phosphors.

Cooperative Near-Infrared Quantum Cutting in Tb3+, Yb3+ Codoped Polyborates La0.99−xYbxBaB9O16:Tb0.01

Near-infrared Quantum Cutting in YPO4:Yb3+, Tm3+ Via Cooperative Energy Transfer

Near Infrared Quantum Cutting in Yb3+-Doped Nay(Wo4)(2) Phosphor with A High Quenching Concentration

Multiphoton near-infrared quantum cutting luminescence phenomena of Tm3+ ion in (Y1-xTm(x))3Al5O12 powder phosphor.

Microstructure and Luminescence of Yb3+-doped Fluorosilicate Glass Ceramics

Two-photon, Three-Photon, and Four-Photon Excellent Near-Infrared Quantum Cutting Luminescence of Tm3+ Ion Activator Emerged in Tm3+:YNbO4 Powder Phosphor One Material Simultaneously

Broadband Three-Photon Near-Infrared Quantum Cutting in Tm3+ Singly Doped YVO4

Quantum Cutting Downconversion by Cooperative Energy Transfer from Bi 3+ to Yb 3+ in Y 2 O 3 Phosphor

Near-Infrared Luminescence of Tb3+-Yb3+ and Ce3+-Yb3+ Co-Doped Y3al5o12

Infrared Quantum Cutting in Tb3+,Yb3+ Codoped Transparent Glass Ceramics Containing CaF2 Nanocrystals

Sensitized Yb3+ Luminescence of Eu3+/Yb3+‐Codoped Fluorosilicate Glass Ceramics

Sensitized Intense Near-Infrared Downconversion Quantum Cutting Three-Photon Luminescence Phenomena of the Tm(3+) Ion Activator in Tm(3+)Bi(3+):YNbO(4) Powder Phosphor.

Intense ultraviolet upconversion luminescence of Yb3+ and Tb3+ co-doped glass ceramics containing SrF2 nanocrystals

Near-infrared Quantum Cutting in Pr 3+ -Yb 3+ Co-doped Oxyfluoride Glass Ceramics Containing CaF 2 Nanocrystals

Near-Infrared Quantum Cutting in Yb3+ Doped SrMoO4 Phosphors

Broadband Absorption and Near-Infrared Quantum Cutting in Ce 3 + –Tb 3 + –Yb 3 + Co-Doped Y 4 Si 2 O 7 N 2 Phosphor via Energy Transfer