Near-infrared Quantum Cutting in Pr 3+ -Yb 3+ Co-doped Oxyfluoride Glass Ceramics Containing CaF 2 Nanocrystals

Lili Zhang,Jie Xu,Yichen Hu,Guorong Chen,Zhongjian Wang
DOI: https://doi.org/10.1007/s11595-013-0712-7
2013-01-01
Abstract:The Pr3+-Yb3+ co-doped oxyfluoride glass-ceramics containing CaF2 nanocrystals were obtained by thermal treatment on the as-made glasses. The structure of fluoride nanocrystals was investigated. The light-emitting mechanism of Pr3+-Yb3+ in the near infrared region was proposed and the fluorescence lifetime and quantum efficiency was calculated. The results indicate that the main phase in the oxyfluoride glass-ceramics is CaF2 nanocrystal sized at 30 nm. Energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) have proved the incorporation of Pr3+ and Yb3+ into CaF2 nanocrystal lattice. Near-infrared quantum cutting involving Yb3+ 980 nm and 1 015 nm ( 2F5/2 → 2F7/2 ) emission has been achieved upon the excitation of the 3P0 energy level of Pr3+ at 482 nm. The fluorescence lifetime decreases sharply and quantum efficiency increases with increasing Yb3+ concentration, and the optimal quantum efficiency reaches 191%.
What problem does this paper attempt to address?