Effect of Y, Al Co-Doping on Hydrogen Storage Properties of La–Mg–Ni-Based Alloys
Guanjiu Wu,Yichao Xie,Yuan Li,Qing Wang,Chenfeng Fan,Wenfeng Wang,Lu Zhang,Shumin Han
DOI: https://doi.org/10.1007/s40195-024-01709-w
2024-06-01
Acta Metallurgica Sinica (English Letters)
Abstract:La–Mg–Ni-based hydrogen storage alloys have excellent hydrogen storage properties. This work reports the hydrogen storage performance of a series of A 2 B 7 -type La 0.96 Mg 0.04 Ni 3.34 Al 0.13 alloy and La 0.96- x Y x Mg 0.04 Ni 3.47–0.6 x Al 0.6 x ( x = 0, 0.22, 0.33, 0.44) alloys, and explores the effect of Y and Al element combined substitution on the microstructure and hydrogen storage performance of A 2 B 7 -type La–Mg–Ni-based alloys. The alloys are composed of Ce 2 Ni 7 phase and LaNi 5 phase. With the increase of x , the cell volume of Ce 2 Ni 7 phase decreases, while that of LaNi 5 phase increases, indicating that Y atom mainly enters Ce 2 Ni 7 phase and Al atom mainly enters LaNi 5 phase. An appropriate amount of co-substitution increases the hydrogen storage capacity and reduces the hydrogen absorption/desorption plateau pressure hysteresis of the alloy. When x = 0.44, the hydrogen storage capacity of the alloy is 1.449 wt%, and the hysteresis coefficient is 0.302. The cell volume of Ce 2 Ni 7 phase and LaNi 5 phase expands to different degrees after 20 absorption/desorption cycles. With the increase of x , the volume expansion rate decreases, and the cycle capacity retention rate also gradually decreases. This is related to the amorphization of Ce 2 Ni 7 phase. When x = 0.22, the capacity retention rate of the alloy is 91.4%.
metallurgy & metallurgical engineering