Abstract:Nanosized Yb(3+) and Er(3+) co-doped β-NaYF4 cores coated with multiple β-NaYF4 shell layers were synthesized by a solvothermal process. X-ray diffraction and scanning electron microscopy were used to characterize the crystal structure and morphology of the materials. The visible and near-infrared spectra as well as the decay curves were also measured. A 40-fold intensity increase for the green upconversion and a 34-fold intensity increase for the red upconversion were observed as the cores are coated with three shell layers. The origin of the upconversion enhancement was studied on the basis of photoluminescence spectra and decay times. Our results indicate that the upconversion enhancement in the sandwiched structure mainly originates from the suppression of de-excitation of Yb(3+) ions. We also explored the population of the Er(3+4)F9/2 level. The results reveal that energy transfer from the lower intermediate Er(3+4)I13/2 level is dominant for populating the Er(3+4)F9/2 level when the nanocrystal size is relatively small; however, with increasing nanocrystal size, the contribution of the green emitting Er(3+4)S3/2 level for populating the Er(3+4)F9/2 level, which mainly comes from the cross relaxation energy transfer from Er(3+) ions to Yb(3+) ions followed by energy back transfer within the same Er(3+)-Yb(3+) pair, becomes more and more important. Moreover, this mechanism takes place only in the nearest Er(3+)-Yb(3+) pairs. This population route is in good agreement with that in nanomaterials and bulk materials.

Microstructure and environment dependence of 2H11/2 --> 4I15/2 upconversion emission in YVO4:Er3+, Yb3+ nanocrystals.

Microstructure and Environment Dependence of <sup>2</sup>H<sub>11/2</sub> → <sup>4</sup>I<sub>15/2</sub> Upconversion Emission in YVO<sub>4</sub>:Er<sup>3+</sup>, Y b<sup>3+</sup> Nanocrystals

Optical Spectroscopy and Visible Upconversion Studies of Yvo4 : Er3+ Nanocrystals Synthesized by A Hydrothermal Process

Synthesis and characterization of Y 2O 3:Er 3+ upconversion materials with nanoporous structures

High-purity and Color-tunable Up-conversion Luminescence of YVO4∶ Yb3 +,er 3 + Nanoparticles

Importance of suppression of Yb(3+) de-excitation to upconversion enhancement in β-NaYF4: Yb(3+)/Er(3+)@β-NaYF4 sandwiched structure nanocrystals

Importance of Suppression of Yb3+ De-Excitation to Upconversion Enhancement in Β-Nayf4: Yb3+/Er3+@β-NaYF4 Sandwiched Structure Nanocrystals

Upconversion Emission and Its Color Modulation of the YVO4: Er3+, Yb3+, Cr3+ Nanoparticles

Size-Dependent Upconversion Luminescence in Er3+/Yb3+-Codoped Nanocrystalline Yttria: Saturation and Thermal Effects

Tunable Upconversion Emission in Ba2YF7:Yb3+/Er3+ Nanocrystals with Different Yb3+ Concentration

Enhancement of Violet and Ultraviolet Upconversion Emissions in Yb3+/Er3+-codoped YF3 Nanocrystals

The Preparation and the Up and Down-Conversion Luminescence of Y_2O_2S∶Er,Yb Nanocrystals

Investigation of Up-conversion on Nanocrystal and Bulk La2O3: (yb3+, Er3+)

The Enhancement of 1.5 μm near infrared luminescence in Er3+ and Yb3+ codoped Y2O3 nanocrystalline

Upconversion luminescence properties of YF3:Yb3+, Er3+ nanoclusters.

pH value manipulated phase transition, microstructure evolution and tunable upconversion luminescence in Yb(3+)-Er(3+) codoped LiYF4/YF3 nanoparticles

Upconversion Mechanisms and Thermal Effects of Er3+ in Er3+ Doped Yttria Nanocrystals

[The enhancement of 1.5 microm near infrared luminescence in Er3+ and Yb3+ codoped Y2O3 nanocrystalline].

Composition tuning the upconversion emission in NaYF4:Yb/Tm hexaplate nanocrystals.

Near-infrared to visible upconversion in Er 3+ and Yb 3+ codoped Lu 2O 3 nanocrystals: Enhanced red color upconversion and three-photon process in green color upconversion

Crystalline Phase and Morphology Controlling to Enhance the Up-Conversion Emission from NaYF4:Yb,Er Nanocrystals