Abstract:The surface modification of bioglass was performed, and after its characterization, its effectiveness was evaluated. Physical characterization and cell adhesion were demonstrated by scanning electron microscope (SEM) technique. Histopathological sections were examined under a light microscope to evaluate the tissue‐material interaction. Bioglasses are solid materials consisted of sodium oxide, calcium oxide, silicon dioxide and phosphorus in various proportions and have used in bone tissue engineering. There have been ongoing efforts to improve the surface properties of bioglasses to increase biocompatibility and performance. The aim of the present study is to modify the bioglass surface with an amino acid mixture consisting of arginine, aspartic acid, phenylalanine, cysteine, histidine and lysine, to characterize the surface, and to evaluate the performance and biocompatibility in vitro and in vivo. The untreated bioglass, bioglass kept in simulated body fluid (SBF), and modified bioglass were used in further evaluation. After confirmation of the surface modification with FT‐IR analyses and SEM analyses, MC3T3‐E1 preosteoblasts adhesion on the surface was also revealed by SEM. The modified bioglass had significantly higher ALP activity in colorimetric measurement, rate of calcium accumulations in Alizarin red s staining, lower rate of cell death in Annexin‐V/PI staining to determine apoptosis and necrosis. Having higher cell viability rate in MTT test and absence of genotoxicity in micronucleus test (OECD 487), the modified bioglass was further confirmed for biocompatibility in vitro. The results of the rat tibial defect model revealed that the all bioglass treatments had a significantly better bone healing score compared to the untreated negative control. However, the modified bioglass exhibited significantly better bone healing efforts especially during the first and the second months compared to the other bioglass treatment treatments. As a result, the amino acid surface modification of bioglasses improves the surface biocompatibility and osteogenic performance that makes the amino acid modified bioglass a better candidate for bone tissue engineering. Research Highlights Bioglass surface modification with amino acids contributes to bioglass‐tissue interaction with an improved cell attachment. Modified bioglass increases in vitro Alp activity and calcium accumulation, and also positively affects cell behavior by supporting cell adaptation. Bioglass exerts osteogenic potential in vivo especially during early bone healing.

Bone bonding in bioactive glass ceramics combined with bone matrix gelatin.

Biphasic ceramic biomaterials with tunable spatiotemporal evolution for highly efficient alveolar bone repair

Bonding of Chemically Treated Titanium Implants to Bone.

Promotion of Osteogenic Differentiation of Stem Cells and Increase of Bone-Bonding Ability in Vivo Using Urease-Treated Titanium Coated with Calcium Phosphate and Gelatin

In Vivo Evaluation of Bone-Bonding Ability of RGD-coated Porous Implant Using Layer-by-layer Electrostatic Self-Assembly.

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

Composition control in biphasic silicate microspheres on stimulating new bone regeneration and repair of osteoporotic femoral bone defect

Bone Responses to Rough Titanium Implants Coated with Biomimetic Ca-P in Rabbit Tibia.

[High Bioactive Material-Bone Graft in Bone Defect Healing]

In Vivo Comparison of Bone Formation on Titanium Implant Surfaces Coated with Biomimetically Deposited Calcium Phosphate or Electrochemically Deposited Hydroxyapatite

Bioactive Pore-Forming Bone Adhesives Facilitating Cell Ingrowth for Fracture Healing

Study on adhesion, proliferation and differentiation of osteoblasts promoted by new absorbable bioactive glass injection in vitro

Enhance the Bioactivity and Osseointegration of the Polyethylene‐Terephthalate‐Based Artificial Ligament via Poly(Dopamine) Coating with Mesoporous Bioactive Glass

Amino acid surface modified bioglass: A candidate biomaterial for bone tissue engineering

A bioactive glass functional hydrogel enhances bone augmentation via synergistic angiogenesis, self-swelling and osteogenesis

Local bone metabolism balance regulation via double-adhesive hydrogel for fixing orthopedic implants

[Nano-Sized Bioactive Glass Enhances Osteogenesis of Critical Bone Defect in Rabbits].

Role of in-situ electrical stimulation on early-stage mineralization and in-vitro osteogenesis of electroactive bioactive glass composites

Bone Adhesives: Bioactive Pore‐Forming Bone Adhesives Facilitating Cell Ingrowth for Fracture Healing (adv. Mater. 10/2020)

The role of hydrated silica, titania, and alumina in inducing apatite on implants

Bone Tissue Engineering by Using Calcium Phosphate Glass Scaffolds and the Avidin–Biotin Binding System