Abstract:A water-based route has been demonstrated for synthesizing ZnSe and Cd-doped ZnSe (ZnSe(ZnxCd1-xSe, 0 < x < 1) quantum dots (QDs) that have tunable and narrow photo luminescence (PL) peaks from the ultraviolet A (UVA) to the blue range (350-490 nm) with full-width at half-maximum (fwhm) values of 24-36 nm. Hydrazine (N2H4) was used to maintain oxygen-free conditions, allowing the reaction vessel to be open to air. The properties of the QDs were controlled using the thiol ligands, 3-mercaptopropionic acid (MPA), thiolglycolic acid (TGA), and L-glutathione (GSH). On the basis of optical spectra, linear three-carbon MPA attenuated nucleation and growth, yielding small ZnSe QDs with a high density of surface defects. In contrast, TGA and GSH produced larger ZnSe QDs with lower surface defect densities. The absorption spectra show that growth was more uniform and better controlled with linear two-carbon TGA than branched bifunctional GSH. After 20 min of growth TGA-capped ZnSe had an average diameter of 2.5 nm based on high-resolution transmission electron microscopy images; these nanocrystals had an absorbance peak maximum of approximately 340 nm (3.65 eV) and a band gap PL emission peak at 372 nm (3.34 eV). Highly fluorescent ZnxCd1-xSe QDs were fabricated by adding a Cd-thiol complex directly to ZnSe QD solutions; PL peaks were tuned in the blue range (400-490 nm) by changing the Zn to Cd ratio. The Cd-bearing nanocrystals contained proportionally more Se based on X-ray photoelectron spectroscopy, and Cd-Se bonds had ionic character, in contrast to primarily covalent Zn-Se bonds.

Synthesis of highly luminescent Mn:ZnSe/ZnS nanocrystals in aqueous media.

Synthesis of Highly Emissive Mn-Doped ZnSe Nanocrystals without Pyrophoric Reagents

Microwave-Assisted Aqueous Synthesis of Transition Metal Ions Doped Znse/Zns Core/Shell Quantum Dots with Tunable White-Light Emission

Synthesis of Highly Luminescent Mercaptosuccinic Acid-Coated Cdse Nanocrystals under Atmospheric Conditions

Enhanced Photoluminescence and Characterization of Mn-Doped Zns Nanocrystallites Synthesized in Microemulsion

Hydrothermal Synthesis of Mn-Doped Znse Quantum Dots and Effects of Surface Overcoating on Their Optical Properties

Enhanced luminescence of ZnSe:Eu 3+/ZnS core-shell quantum dots

Facile synthesis, optical properties and growth mechanism of elongated Mn-doped ZnSe1-xSx nanocrystals

Authorship in a small medical journal: A study of contributorship statements by corresponding authors

Enhanced luminescence using the core‐shell‐shell structure of 3‐mercaptopropionic acid‐capped ZnSe/ZnS: Mn/ZnS quantum dot

Photo-assisted synthesis of highly fluorescent ZnSe(S) quantum dots in aqueous solution

Efficient and Color-Tunable Mn-Doped Znse Nanocrystal Emitters: Control of Optical Performance Via Greener Synthetic Chemistry

Phosphine-free Synthesis of High Quality ZnSe, ZnSe/ZnS, and Cu-, Mn-doped ZnSe Nanocrystals.

Facile Hydrothermal Synthesis of Mn Doped ZnS Nanocrystals and Luminescence Properties Investigations

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

Synthesis And Characterization Of Water-Soluble Cdse/Zns Core-Shell Nanoparticles

Water-Soluble Cdse and Cdse/Cds Nanocrystals: A Greener Synthetic Route

Highly Luminescent and Photostable Core/Shell/Shell ZnSeS/Cu:ZnS/ZnS Quantum Dots Prepared via a Mild Aqueous Route

High Quality ZnSe and ZnS Nanocrystals Formed by Activating Zinc Carboxylate Precursors

Synthesis and Luminescent Modulation of ZnS Crystallite by a Hydrothermal Method

Synthesis and Characterization of High-Quality Colloidal Mn2+-Doped Zns Nanoparticles