Abstract:In recent years, more than 6 million room temperature vulcanized (RTV) silicone rubber coated cap and pin insulators with high mechanical ratings were used in ultrahigh voltage transmission lines in China to improve pollution performance. However, the unexpected puncture phenomena of RTV coated insulators were exposed during steep-front impulse voltage tests; for instance, the steep-front impulse voltage test pass rate decreased to less than 50% for 550 kN glass insulators with RTV coatings. The steep-front impulse voltage test is the most effective method used to check the insulation quality of cap and pin insulators. This unexpected phenomenon once caused serious concerns to power utilities. In this paper, several possible factors that affect the puncture of insulators were analyzed. Then, the extent of the decline in the breakdown of the 550 kN glass cap and pin insulators with and without RTV coatings were studied. The initial puncture location was then found, and the developmental process of the arc on the insulator surface in steep-front impulse voltage tests was observed with an ultra-high-speed intensified charge coupled device camera. Lastly, a breakdown mechanism is proposed. The puncture phenomena of a RTV coated insulator in a steep-front impulse voltage test is essentially an electrical breakdown of the internal insulation. The RTV coating induces the close adherence of the arc to the surface of the insulator. Such closeness changes the arc development path on the insulator surface and facilitates easy breakdown in the shed weak part. All these factors result in a significant increase in the breakdown probability of RTV coated insulators in steep-front impulse voltage tests.

Durability of RTV-coated Insulators Used in Subtropical Areas

Analysis on Operating Performance of RTV Coated Insulators Used in Dry Area

Field Aging Investigation and Filler Precipitation Analysis on Rtv Coated Insulators in China

Evaluation of Long-term Performance of Composite Insulators for ±400kv Overhead Line on Tibet Plateau

Application of Pre-Coated Rtv Insulators in Uhv Ohls and Steep-Front Impulse Voltage Test

AGING STUDY ON RTV COATING COVERED ON INSULATORS AND ENERGIZED FOR MANY YEARS

Investigation on Field-Aged RTV-Coated Insulators Used in Heavily Contaminated Areas

Test On Modified Rtv Coating For Hot And Humid Environment

Characteristics of Three Kinds of Insulators and Their Applications Evaluation at Them in UHV Transmission Lines

Thermal and Voltage Distribution along Insulator Strings with Semiconducting Rtv Coatings

Study on Selection Method of External Insulation and Insulator Type Selection for 750 Kv Transmission and Transformation Equipment in High Altitude Area

The Developments of Room Temperature Vulcanized Silicone Rubber Coating and Its Application in China

Insulation Coordination of UHVDC Transmission Line

Non-destructive Condition Assessment of Silicone Rubber Composite Insulators

Puncture Phenomena and Mechanism Analysis of a RTV Coated Cap and Pin Insulators in a Steep-Front Impulse Voltage Test

5000 h multi-stress test procedure for silicone rubber composite insulators and its applications in long-term performance evaluation

Pollution Flashover Performance of 220kv Glass Insulator Strings Covered with Incomplete Spraying Prtv Coatings

Development of Composite Insulators in China

Influence of Algae Growth on the Electrical Performance of RTV Coated Post Insulators

Investigation on Hydrophobicity and Pollution Status of Composite Insulators in Contaminated Areas

Pollution Flashover Performance of RTV Coatings with Partial Damage