Effect of Fe/Ni Ratio on Amorphization, Crystallization Kinetics, and Magnetic Properties of FeNiSiBCuNb Alloys
Zhe Chen,Shujie Kang,Qianke Zhu,Kewei Zhang,Jifan Hu,Yong Jiang
DOI: https://doi.org/10.1016/j.jnoncrysol.2022.121842
IF: 4.458
2022-01-01
Journal of Non-Crystalline Solids
Abstract:In this work, the precipitation phase transformation, crystallization kinetics, and soft magnetic properties of (FexNi80-xSi9.5B9.5Cu1)(0.97)Nb-0.03 (x = 36, 38, 40, 42, 44) alloys have been investigated systematically. It was found that the partial substitution of Fe for Ni can enhance the GFA, increasing the T-rg from 0.507 to 0.527 for the best-performing alloy. With increasing annealing temperature, less alpha-Fe(Si), and more (Fe,Ni)Si and (Fe,Ni)B phase precipitates. The crystallization kinetics show that the peak temperature of the secondary phase transformation (alpha-Fe(Si)->gamma(Fe,Ni)Si) is less sensitive to the heating rate. It is also found that structural relaxation of the amorphous system and consequential release of internal stress results in a decrease in H-c and an increase in mu(e). The minimum H-c values and maximum mu(e) values for the alloys with x = 36, 38, 40, 42, and 44 were 0.14 A/m, 0.11 A/m, 0.23 A/m, 0.08 A/m, and 0.03 A/m, and 17,000, 14,600, 10,800, 12,700, and 16,500, respectively.