Low-Loss Composite NiCuZnCo–BaTiO3 With Matched Permeability and Permittivity in High Frequency Range

Tianshui Zhang,Hua Su,Xiaoli Tang,Huaiwu Zhang

DOI: https://doi.org/10.1109/TMAG.2014.2327953

2014-01-01

Abstract:The magnetic and dielectric properties of the composites Ni0.35Cu0.18Zn0.45Co0.02Fe1.95O4 + x wt% BaTiO3(x = 0, 5, 10, 15, 20, 25) were investigated. All samples were sintered at 1080 °C for 3 h to obtain approximately equal real permeability and permittivity. X-ray diffraction results indicated that there had no obvious reaction between the NiCuZnCo ferrite and the BaTiO3 in all samples. BaTiO3 powder could obviously suppress grain growth of the composites. The sample Ni0.35Cu0.18Zn0.45Co0.02Fe1.95O4 + 15 wt% BaTiO3 presented a real permeability of ~29 (loss tangent ~0.02) and a real permittivity of ~28.3 (loss tangent ~0.002), respectively, over 3-30 MHz. This composite material had potential prospects in antenna miniaturization at HF band (3-30 MHz).