Abstract:MnZn power ferrites were prepared by conventional oxide ceramic process.The influence of ZnO content on the temperature dependence of initial permeability(μi) and losses of MnZn power ferrites were investigated by means of characterizing the fracture surface micrograph,electrical resistivity,magnetic properties and density.The results indicated that at room temperature,all of the density,initial permeability,saturation magnetic induct ion and electrical resistivity of MnZn power ferrites all increased initially and then decreased with the increase of ZnO content,while the losses decreased first and increased subsequently,and Curie temperature decreased monotonously.Meanwhile,the temperature of secondary maximum peak of μi-T curve and the minimum losses temperature moved to lower temperature while the ZnO content increased.When the content of ZnO was 14.5%,the initial permeability,saturation magnetic induction,density and electrical resistivity reached their maxima,while the hysteresis loss(Ph),eddy current loss(Pe) and the total losses(Pcv) achieved their minima.The Ph-T and μi-T curves varied contrarily,and due to the contribution of extral eddy current loss(Pe,exc) which was proportional to Ph,the Pe-T curve did not agree with its classical expression.Finally,when the content of ZnO was 14.0%,MnZn ferrite with high initial permeability(3 180) at room temperaturer and low losses(280～350 kW/m3) within wide temperature range of 25～120 ℃ has been obtained.

Influence of Second Milling Time on Temperature Dependence of Low Loss MnZn Power Ferrites

Influences of Second Milling Time on Microstructure and Magnetic Properties of MnZn Ferrites

Effects of ZrO2 Addition on the Temperature Dependence of MnZn Power Ferrites

Effects of Fe2+ content in raw materials on Mn–Zn ferrite magnetic properties

Influence of ZnO Stoichiometry on Temperature Dependence of Magnetic Properties in MnZn Power Ferrites

Analysis of High Frequency Power Loss of MnZn Power Ferrite

Effect of ZnO on the Temperature Dependence of Initial Permeability and Losses of MnZn Ferrites

A Study of Sintering of High Frequency MnZn Power Ferrite

Influence Of Fe2o3 Stoichiometry On Initial Permeability And Temperature Dependence Of Core Loss In Mnzn Ferrites

Effect of Sintering on the Properties of Low Power Loss Doped MnZn Ferrites

Temperature Characteristics of Core Losses for HfO2 Doped Manganese-Zinc Ferrites

Temperature and Frequency Characteristics of Low-Loss MnZn Ferrite in a Wide Temperature Range

Temperature Dependence of Core Losses at High Frequency for Mnzn Ferrites

Research and Development of Low-loss MnZn Power Ferrites in Wide-temperature

Magnetic and dielectric properties of low‐loss MnZn ferrites with wide temperature stability

Effects of magnetic domain morphology on the magnetic spectrum and high‐frequency core losses of MnZn ferrites

Effects of Microstructure on the Temperature Dependence of Relative Initial Permeability of NiCuZn Ferrites

Influence of ${\hbox{fe}}_{2}{\hbox{o}}_{3}$ Stoichiometry on Initial Permeability and Temperature Dependence of Core Loss in MnZn Ferrites

Effects of Sintering Temperature on the Magnetic Properties of Power NiZn Ferrite

Low temperature sintered MnZn ferrites for power applications at the frequency of 1 MHz

Research Advancements and Developing Trends of MnZn Power Ferrites